The invention discloses a concrete water reducing agent, belonging to the technical field of concrete additives. The present invention with ethyl acetate and thionyl chloride as the reaction protective solution by methylsulfonic acid and two methyl formamide as raw material, through the preparation of thionyl chloride modified methanesulfonyl chloride, allyl alcohol, benzene acetic acid and then mixed reaction, modified liquid, and then in the synthesis process of poly carboxylic acid. The modified solution of polycarboxylic acid modified with sulfonic group, amide group and amino group, increase the water reducing efficiency, so as to obtain the concrete water reducing agent, the prepared water reducing agent and water reducing efficiency, and cement to good performance, to improve its physical properties, and has broad application prospects the.
【技术实现步骤摘要】
一种混凝土减水剂及其制备方法
本专利技术公开了一种混凝土减水剂及其制备方法，属于混凝土添加剂
技术介绍
混凝土减水剂是指在混凝土和易性、水泥用量不变的条件下，能减少拌合用水量的外加剂，其通过表面活性作用、络合作用、静电排斥力或立体排斥力等阻碍或破坏颗粒的絮凝结构，从而能够在节约水泥用量的同时，保证混凝土的和易性及强度。由于水泥化学组成、掺合料、混凝土配合比、水灰比等要素的多变性，使得混凝土减水剂的使用效果出现差异。减水剂是目前使用最为广泛的一种混凝土添加剂，按照减水率大小可将混凝土减水剂分为普通减水剂、高效减水剂。高效减水剂具有高减水率和使用后混凝土具有优良的性能，主要是石化产品和合成产品，成本高。而作为普通减水剂代表的木质素磺酸盐，其减水率为8%左右，可以直接使用，也可作为复合型外加剂原料之一，因其价格较便宜，使用较为广泛。目前已利用落叶松栲胶树皮废渣、玉米芯、玉米秆、麦草、稻草等原料开发出了混凝土减水剂，其产品造价低，性能也因原料不同存在差异，均可满足不同减水产品的要求。可是，传统的减水剂产品多为甲醛缩合物，典型的有萘磺酸甲醛缩合物减水剂、磺化三聚氰...
【技术保护点】
一种混凝土减水剂，其特征在于：由如下重量份数计的原料组成，116～123份烯丙基聚氧乙烯醚、92～98份丙烯酸、60～70份混合料、36～42份丙烯醇、14～16份苯乙烯、4～7份酒石酸、2.9～3.6份过硫酸铵及1.8～2.5份巯基丙酸。
【技术特征摘要】
1.一种混凝土减水剂，其特征在于：由如下重量份数计的原料组成，116～123份烯丙基聚氧乙烯醚、92～98份丙烯酸、60～70份混合料、36～42份丙烯醇、14～16份苯乙烯、4～7份酒石酸、2.9～3.6份过硫酸铵及1.8～2.5份巯基丙酸。2.根据权利要求1所述的一种混凝土减水剂，其特征在于：所述混合料的制备包括以下步骤：A.按质量比1:3，取乙酸乙酯和氯化亚砜放入反应器中搅拌均匀，再分别加入氯化亚砜质量30～35%的甲磺酸和氯化亚砜质量2～3%的二甲基甲酰胺，设定温度为88～93℃，搅拌混合；B.在搅拌混合后，使用滴液漏斗向反应器中滴加亚硫酰氯，滴加速率为每三秒一滴，滴加量为甲磺酸质量的1.2～1.5倍，待亚硫酰氯滴加完成后，升温至102～105℃，保温10～15min；C.待保温结束后冷却至室温，将反应器中的物质移入蒸馏装置中，通过减压蒸馏回收氯化亚砜，收集剩余物，将剩余物与剩余物质...
【专利技术属性】
技术研发人员：陈建乐，宋昊，李雪晴，
申请(专利权)人：常州聚盛节能工程有限公司，
类型：发明
国别省市：江苏,32