The invention relates to a water-based coating composition of the following components: 21 water, 4 51% 13% C110, 2 6% diatomite calcined alumina, 0.3 2%, 16 hexandiol 47% elastomer acrylic resin, 0.7 3% acrylic thickener and 0.7 3% ammonium hydroxide. Preferably, composition optionally contains the following components, to provide insulation, corrosion inhibition, self extinguishing properties, impermeability, epoxy and ecological: 2 6% 4 13% titanium dioxide, precipitated calcium carbonate, 2 6%, 0.3, 0.3 2%texanol DBP 2% fungicides and 0.3 2% defoaming agent. Through these ranges, the application of various compositions for research and development of insulation, corrosion inhibition, self extinguishing, impermeable, epoxy and ecological coatings can be covered.
【技术实现步骤摘要】
【国外来华专利技术】
本专利技术涉及绝缘性、腐蚀抑制性、自熄性、不可渗透性、环氧且生态的水基涂料组合物，并且该水基涂料组合物具有多种工业用途。
技术介绍
在现有技术中存在许多涂料组合物，其提供许多性能，例如阻燃性、耐腐蚀性、耐热性、耐水性或耐酸性或耐碱性。例如，欧洲专利申请EP0583051A1教导了一种具有阻燃性、耐腐蚀性、耐热性和耐酸性或耐碱性的性能的水基涂料组合物，但是具有非常有限的应用和热导率、热膨胀、耐候性和环保性能，更不用说其成本高，由昂贵的原材料组成，需要复杂的混合技术，并且由于其特殊且有限的组成和制造方法，产生矿物和冶金废物，包括在碱金属硅酸盐水溶液中的耐热二氧化硅和硅酸铝以及耐热金属氧化物。同样地，美国专利申请US2008/0233295A1教导了一种具有非常有限的应用和热导率、热膨胀、耐候性和环保性质的抗氧化涂料组合物，更不用说其高成本，由昂贵的原材料组成，需要复杂的混合技术，并且由于其特殊且有限的组成和制造方法，产生矿物和冶金废物，包括基于锰矿物、冶金固体废物、铝粉、有机增稠剂和无机粘合剂的混合物而制备的糊料。最后，美国专利申请US5,612,130教导了具有耐...
【技术保护点】
用作绝缘性、腐蚀抑制性、自熄性、不可渗透性、环氧且生态涂料的组合物，其包含：21‑51％水，4‑13％硅藻土C110(Celite)，2‑6％煅烧氧化铝，0.3‑2％己二醇，16‑47％弹性体丙烯酸树脂，0.7‑3％丙烯酸增稠剂，和0.7‑3％氢氧化铵。
【技术特征摘要】
【国外来华专利技术】1.用作绝缘性、腐蚀抑制性、自熄性、不可渗透性、环氧且生态涂料的组合物，其包含：21-51％水，4-13％硅藻土C110(Celite)，2-6％煅烧氧化铝，0.3-2％己二醇，16-47％弹性体丙烯酸树脂，0.7-3％丙烯酸增稠剂，和0.7-3％氢氧化铵。2.根据权利要求1所述的组合物，其进一步包含2-6％二氧化钛。3.根据...
【专利技术属性】
技术研发人员：莫埃斯·菲格罗亚·马丁内斯，
申请(专利权)人：墨西哥G卡瓦尔可变动资本额公司，
类型：发明
国别省市：墨西哥;MX