With filter lens and method for preparation of welding method, the lens material for resin lens material and dispersed in the core-shell structure of iron oxide, titanium oxide and copper oxide nanoparticles; wherein, the total accounted for 0.5% of the total weight of nanoparticles to resin lens material 3.5%, iron oxide, titanium oxide and copper oxide nanoparticles to weight ratio of 1.8 to 2.1: 1.8 to 2.1: 0.9 to 1.1; the nanoparticles as the core of iron oxide, titanium oxide and copper oxide, the particle size of 10-50nm; the shell as the surface modification agent or surface modifier, the thickness is 3-10nm. The resin filter lens can not only see the workpiece before the arc, but also can filter harmful light after the arc, and protect the eyes.
【技术实现步骤摘要】
本专利技术涉及一种电焊用护目滤光镜片，具体为利用高分子树脂与纳米粒子复合制造的功能性树脂滤光片。
技术介绍
滤光片是一种光学材料，是用来拦截或选择性滤过某些波段光线的光学器件，能衰减光强度和改变光成分，它通常是由塑料片或玻璃片再加入特种染料制作而成，作为各种设备或器材的窗口材料。日常使用的电焊防护滤光镜片，大多为玻璃晶体结构镜片，由于玻璃镜片透过率较低，电焊操作员在起焊前根本无法看见被焊工件，焊接过程中，视物也模糊，影响焊接质量和速度，特别是在光线较弱的特殊作业场所或焊接精密度要求较高的工件，影响更大。究其原因主要是现有电焊防护镜片在过滤有害强光的同时，也影响到无害光线的通过，特别是在光线较弱的特殊场所，由于镜片在可见光区透过率过低，造成视物不清楚。因此如何使操作人员起焊前就能通过弱谱线区域的高透过率观察到工件的具体位置，从而对准部位进行焊接，显得尤为重要。
技术实现思路
本专利技术针对现有技术的不足，提出了一种电焊用滤光镜片及其制造方法，通过该方法制备的树脂滤光镜片不仅在起弧前能看清工件，起弧后仍能过滤有害强光，保护眼睛。<...
【技术保护点】
一种电焊用滤光镜片，其特征在于，该镜片的材料为树脂镜片材料以及分散于其中的核壳结构氧化铁、氧化钛和氧化铜纳米粒子；其中，该纳米粒子总量占树脂镜片材料总重量的0.5％～3.5％，氧化铁、氧化钛和氧化铜纳米粒子的重量比为1.8～2.1∶1.8～2.1∶0.9～1.1；该纳米粒子的内核为氧化铁、氧化钛和氧化铜，粒径为10‑50nm；外壳为表面修饰剂或表面改性剂，厚度为3‑10nm。
【技术特征摘要】
1.一种电焊用滤光镜片，其特征在于，该镜片的材料为树脂镜片材料以及分
散于其中的核壳结构氧化铁、氧化钛和氧化铜纳米粒子；其中，该纳米粒子总量
占树脂镜片材料总重量的0.5％～3.5％，氧化铁、氧化钛和氧化铜纳米粒子的重量
比为1.8～2.1∶1.8～2.1∶0.9～1.1；该纳米粒子的内核为氧化铁、氧化钛和氧化铜，
粒径为10-50nm；外壳为表面修饰剂或表面改性剂，厚度为3-10nm。
2.如权利要求1所述的电焊用滤光镜片，其特征在于，所述树脂镜片材料为
聚甲基丙烯酸甲脂或烯丙基乙二醇酸脂。
3.如权利要求1或2所述的电焊用滤光镜片，其特征在于，所述表面修饰剂
或表面改性剂为C2-C5羧酸盐、聚乙烯基吡咯烷酮或十二烷基苯磺酸钠。
4.一种电焊用滤光镜片的制备方法，其特征在于，该方法包括如下步骤：
(1)聚合反应：按照权利要求1所述配比将纳米粒子分散溶解在作为树脂镜
片材...
【专利技术属性】
技术研发人员：王旭，王明华，徐静涛，李国栋，郑永华，薛晓花，
申请(专利权)人：江苏华天通科技有限公司，
类型：发明
国别省市：江苏;32