The invention belongs to the field of polymer materials, in particular relates to a plastic auto parts with ceramic powder modified nylon 66 material, the material by weight of raw material: nylon 66100, three fluorine propyltrimethoxysilane, 2-3 ceramic powder 10-12, castor oil, phthalic acid two 2-4 two 6-8, 3-5, octyl ammonium molybdate 14-17 barium sulfate and ethylsiloxane 2-3 and auxiliary 12-15; the invention uses ceramic powder and other raw materials of nylon 66 was modified, which has good mechanical properties and processing properties of the prepared materials, strong wear, heat aging, high temperature and low temperature, good chemical stability, self lubrication use, safe and reliable, can be widely used for plastic parts for the production of various types of car.
【技术实现步骤摘要】
本专利技术属于高分子材料领域，具体涉及一种汽车塑料件用陶瓷粉改性尼龙66材料及其制备方法。
技术介绍
随着汽车产业的发展，人们对汽车的舒适性、安全性、美观性、节能性等使用性能的要求越来越高，而改进传统汽车用材料，是完善汽车使用性能的根本途径，高分子汽车塑料材料较之传统汽车材料有许多突出的优点，质量轻、机械性能优越、易加工成型，材料可重复利用，还具有卓越的美观装饰作用，然而这些高分子材料也存在一些缺点，比如刚性较差、容易燃烧、不耐高温低温老化等等，因此，为了提高传统高分子材料的性能，拓宽材料使用范围，需要改进原有汽车用塑料配方，对材料进行改性处理，使其能广泛的应用于汽车各个部位。
技术实现思路
本专利技术的目的在于，提供一种汽车塑料件用陶瓷粉改性尼龙66材料，提升了传统尼龙材料的性能，使其具备优良的机械性能，能够适应特定的使用环境，为了实现上述目的，本专利技术采用的技术方案如下：一种汽车塑料件用陶瓷粉改性尼龙66材料，其特征在于，本专利技术材料由以下重量份的原料制成：尼龙66100、三氟丙基三甲氧基硅烷2-3、陶瓷粉10...
【技术保护点】
一种汽车塑料件用陶瓷粉改性尼龙66材料，其特征在于，该材料由以下重量份的原料制成：尼龙66 100、三氟丙基三甲氧基硅烷2‑3、陶瓷粉10‑12、蓖麻油2‑4、邻苯二甲酸二辛酯6‑8、钼酸铵3‑5、硫酸钡14‑17、乙烯基三乙氧基硅烷2‑3、助剂12‑15；所述的助剂由以下重量份的原料制成：粘土300‑320、海泡石粉3‑4、蛭石粉1‑2、1,6己二醇二丙烯酸酯14‑16、蒙脱石粉2‑3、碳酸钠3‑4、氟硅酸钠4‑5、硝酸银1‑2、二硼化钒2.1‑2.4、丁香油1‑2、棕刚玉粉1‑2、硅烷偶联剂KH‑550 1‑2；制备方法是将粘土放入煅烧炉中在710‑740℃下煅烧3‑4...
【技术特征摘要】
1.一种汽车塑料件用陶瓷粉改性尼龙66材料，其特征在于，该材料由以下重量份的原料制成：尼龙66100、三氟丙基三甲氧基硅烷2-3、陶瓷粉10-12、蓖麻油2-4、邻苯二甲酸二辛酯6-8、钼酸铵3-5、硫酸钡14-17、乙烯基三乙氧基硅烷2-3、助剂12-15；
所述的助剂由以下重量份的原料制成：粘土300-320、海泡石粉3-4、蛭石粉1-2、1,6己二醇二丙烯酸酯14-16、蒙脱石粉2-3、碳酸钠3-4、氟硅酸钠4-5、硝酸银1-2、二硼化钒2.1-2.4、丁香油1-2、棕刚玉粉1-2、硅烷偶联剂KH-5501-2...