The invention relates to a novel permeable crystallization plugging agent and construction method, the permeable crystallization plugging agent including the weight ratio of 1.1 to 1.3 liquid and powder; the powder comprises the following group: 90% weight ratio of cement, lime 5%, lithium chloride 2.5%, architectural powder 0.5%, early strength agent 2%; the liquid agent comprises a weight ratio of 10 12 water and water repellent agent, the hydrophobic agent including the following points: the weight ratio of group 10%, 90% silicone methyl silicate. Compared with the prior art, the utility model has the advantages of short final setting time, high early compressive strength, strong impermeability, simple construction procedure, etc., and can be widely used in waterproof systems, such as kitchens, toilets, basements, etc..
【技术实现步骤摘要】
一种新型渗透结晶堵漏剂及施工方法
本专利技术涉及防水涂料
，具体是指一种新型渗透结晶堵漏剂及施工方法。
技术介绍
渗透结晶堵漏剂目前普遍使用的是水泥基渗透结晶型防水剂，水泥基渗透结晶型防水剂是一种含有活性化合物的粉状防水涂料，在有水存在的条件下，活性化合物向混凝土内部渗透，在孔隙和裂缝中形成大量不溶于水的长链状结晶，填表塞毛细孔道，从而使混凝土致密、防水。水泥基渗透结晶型防水剂在厨房、卫生间等建筑内部的防水施工中，主要是用于厨房、卫生间混凝土基层的防水处理。但是当厨房、卫生间混凝土墙面铺贴磁砖之后，出现渗水情况只能将磁砖墙面破坏掉，对混凝土墙面重新做防水处理。此种处理的方式存在：破坏力度大，施工强度高，资金投入大，影响住户正常居住等缺陷。为此诸多企业都将研究的精力投入到在不破坏墙面瓷砖的基础上，实施防水处理的研究当中，最大程度上降低施工强度，减少资金投入。但是目前出现的使用于瓷砖墙面的防水剂，普遍存在终凝时间长、早期抗压强度低、抗渗性能差等缺陷。
技术实现思路
本专利技术针对现有技术的不足，提供一种新型渗透结晶堵漏剂及施工方法。一种新型渗透结晶堵漏剂，包括重量比...
【技术保护点】
一种新型渗透结晶堵漏剂，其特征在于：包括重量比为1.1‑1.3 的液剂和粉剂；所述粉剂包括按重量配比的以下组分：水泥90%、生石灰5%、氯化锂2.5%、建筑胶粉0.5%、早强剂2%；所述液剂包括重量比为10‑12的水和憎水剂，所述憎水剂包括按重量配比的以下组分：甲基硅酸盐10%、有机硅90%。
【技术特征摘要】
1.一种新型渗透结晶堵漏剂，其特征在于：包括重量比为1.1-1.3的液剂和粉剂；所述粉剂包括按重量配比的以下组分：水泥90%、生石灰5%、氯化锂2.5%、建筑胶粉0.5%、早强剂2%；所述液剂包括重量比为10-12的水和憎水剂，所述憎水剂包括按重量配比的以下组分：甲基硅酸盐10%、有机硅90%。2.根据权利要求1所述的一种新型渗透结晶堵漏剂，其特征在于：所述早强剂为三乙醇胺、三异丙醇胺、甲酸钙、尿素、铬酸盐中的任意一种。3.根据权利要求1所述的一种新型渗透结晶堵漏剂，其特征在于：所述水泥为硅酸盐水泥和硫铝酸盐水泥的混合物，硫铝酸盐水泥和硅酸盐水泥重量比为3:1-4:1。4.一种新型渗透结晶堵漏剂的施工方法，其特征在于，包括以下步骤：（1）按重量配比，称取水泥90%、生石灰5%、氯...