一种铜硅焊丝制造技术

本发明专利技术涉及一种铜硅焊丝，按照重量百分比数计算，包括以下原料制成：Sn≤0.06％，Al：1.2～2.5％，Mn：0.25～1％，Si≤5～10％，Cr≤0.015％，Fe≤0.5％，S：0.005～0.015％，Ti：0.8％，B≤0.0006％，W≤0.07％，余量为铜、微量元素和不可避免的杂质。该发明专利技术提高了生产焊丝线坯的效率，且生产的线坯表面光滑，不会被氧化，内部组织均匀，化学成分稳定，杂质元素含量低，线坯具有优良的力学性能，降低了能耗，为线坯的后续拉拔减轻了难度，焊缝不开裂，力学性能好。

Copper silicon welding wire

The invention relates to a silicon copper wire, calculated according to the weight percentage, which comprises the following raw materials: Sn = 0.06%, Al:1.2 ~ 2.5%, Mn:0.25 ~ 1%, Si = 5 ~ 10%, Cr = 0.015%, Fe = 0.5%, S:0.005 ~ 0.015%, Ti:0.8%, B = 0.0006%, W = 0.07%, the balance of copper impurity micro elements and inevitable. The invention improves the efficiency of production line wire billet production line, and the billet surface is smooth, not be oxidized, internal microstructure, chemical stability, low content of impurity elements, wire has excellent mechanical properties, reduces energy consumption, for drawing wire reduce difficult degree, weld cracking, mechanical properties good.

【技术实现步骤摘要】
一种铜硅焊丝
本专利技术涉及一种焊丝钎料，具体是涉及一种铜硅焊丝。
技术介绍
焊丝是作为填充金属或同时作为导电用的金属丝焊接材料。在气焊和钨极气体保护电弧焊时，焊丝用作填充金属；在埋弧焊、电渣焊和其他熔化极气体保护电弧焊时，焊丝既是填充金属。长期以来国内外生产铜硅焊丝的企业都是采用水平连铸工艺生产焊丝线坯，采用此种方法生产的线坯具有规格大、效率低、能耗大、生产周期长、杂质含量高、线坯表面易氧化和内部组织不均匀，组织粗大容易发生缺陷，不利于后续焊丝的拉拔生产等缺点，且在焊丝后续拉拔过程中会进行多次退火，浪费了能源，而且生产的效率也不高。
技术实现思路
本专利技术要解决的技术问题是克服现有技术效率低、能耗大、生产周期长、杂质含量高、线坯表面易氧化和内部组织不均匀的缺陷，提供一种铜硅焊丝。为解决上述技术问题，本专利技术提供以下技术方案：一种铜硅焊丝，按照重量百分比数计算，包括以下原料制成：Sn≤0.06％，Al：1.2～2.5％，Mn：0.25～1％，Si≤5～10％，Cr≤0.015％，Fe≤0.5％，S：0.005～0.015％，Ti：0.8％，B≤0.0006％，W≤0.07％，余量为铜本文档来自技高网...

【技术保护点】
一种铜硅焊丝，其特征在于：按照重量百分比数计算，包括以下原料制成：Sn≤0.06％，Al：1.2～2.5％，Mn：0.25～1％，Si≤5～10％，Cr≤0.015％，Fe≤0.5％，S：0.005～0.015％，Ti：0.8％，B≤0.0006％，W≤0.07％，余量为铜、微量元素和不可避免的杂质。

【技术特征摘要】
1.一种铜硅焊丝，其特征在于：按照重量百分比数计算，包括以下原料制成：Sn≤0.06％，Al：1.2～2.5％，Mn：0.25～1％，Si≤5～10％，Cr≤0.015％，Fe≤0.5％，S：0.005～0.015％，...

【专利技术属性】
技术研发人员：曹立兵，
申请(专利权)人：安徽华众焊业有限公司，
类型：发明
国别省市：安徽,34