The present invention provides by ultrasonic melt spinning method for assembling the assembled six angle of twist drill, which comprises the following steps: 1, surface cleaning and installation; step two, the speed of the design, including the speed of pressing speed and rotating speed; step three, weld design, set the frequency and pressure of ultrasonic hair vibration value; step four, natural cooling, the invention has the advantages of high torque, high efficiency, durable, high practicability, can adjust the speed of time, pressure, also can adjust the semi-automatic or automatic production of applicable scope, to be part of a high speed rotating drive melt by high speed motor, to be the molten surface friction heat, and pressure welding, has the advantages of simple process, high production efficiency.
【技术实现步骤摘要】
一种组装式六角柄麻花钻超声波旋熔装配方法
本专利技术涉及机械装配领域，具体涉及一种组装式六角柄麻花钻超声波旋熔装配方法。
技术介绍
现在广泛使用的组装式六角柄麻花钻主要结构形式分为整体式和分体连接式二种：整体式结构，即组装式六角柄麻花钻的六角柄部分和刃部麻花钻部分采用整体材料，通过机械加工形成，用这种工艺方法生产的产品材料消耗大，生产工艺复杂，因而产品成本高；分体连接式结构，即组装式六角柄麻花钻的六角柄部分和刃部麻花钻部分采用不同材料分别加工后再进行连接，这种结构柄部采用普通材料，少用了刃部昂贵材料的，从而降低成本。目前常用的六角柄麻花钻连接方式是过盈嵌套、径向穿销铆接等方式实现，其连接工艺方法，对半成品六角柄部分和刃部麻花钻部分精度要求高、工艺复杂、生产效率低、连接后的抗扭强度不易保证。
技术实现思路
为了解决现有技术中存在的问题，本专利技术提供了一种组装式六角柄麻花钻超声波旋熔装配方法。本专利技术解决上述问题的技术方案为：一种组装式六角柄麻花钻超声波旋熔装配方法，其具体包括以下步骤：步骤一：表面清洗及安装：室温下对六角柄部分和刃部麻花钻表面进行处理，并利用酒精清洗...
【技术保护点】
一种组装式六角柄麻花钻超声波旋熔装配方法，其特征在于，其具体包括以下步骤：步骤一：表面清洗及安装：室温下对六角柄部分和刃部麻花钻表面进行处理，并利用酒精清洗干净，将清洁过的六角柄部分和刃部麻花钻分别固定在超声波旋熔装置上，分别通过不同的电机带动六角柄部分和刃部麻花钻旋转；步骤二：旋熔设计：设计压合速度以及旋转速度；步骤三：冷却：停止装配，冷却。
【技术特征摘要】
1.一种组装式六角柄麻花钻超声波旋熔装配方法，其特征在于，其具体包括以下步骤：步骤一：表面清洗及安装：室温下对六角柄部分和刃部麻花钻表面进行处理，并利用酒精清洗干净，将清洁过的六角柄部分和刃部麻花钻分别固定在超声波旋熔装置上，分别通过不同的电机带动六角柄部分和刃部麻花钻旋转；步骤二：旋熔设计：设计压合速度以及旋转速度；步骤三：冷却：停止装配，冷却。2.如权利要求1所述的一种组装式六角柄麻花钻超声波旋熔装配方法，其特征在于，所述冷却的冷却过程为自然冷却。3.如权利要求1所述的一种组...