The invention relates to a method for stamping sheet metal, which comprises a metal plate heating will be processed, and coated by weight mixed coating: A lube base oil 30 ~ 40, 5 ~ 10 for petroleum resin, Leather Cream 1 ~ 5 and silicate 0.5 mg ~ 1; and then cooling, and then in coated by weight mixed coating: B lube base oil 30 ~ 40, 5 ~ 10 for petroleum resin, clay 1 ~ 5 and 0.5 ~ 1 silica; the metal plate add to the mold, according to the set pressure to start the stamping press. The invention utilizes the principle of thermal expansion and contraction, sheet metal heating to be treated and coated with special coating material A, and then cooled and coated with special coating material B, so as to overcome the crack or scratch the problems existing in the process of sheet metal stamping.
【技术实现步骤摘要】
金属板材的冲压方法
本专利技术涉及机械零配件加工
，尤其是一种金属板材。
技术介绍
随着金属板材的应用越来越广泛，而金属板材的质量与其冲压方法密切相关，因此，人们对于其冲压方法也越来越关注。目前，在对金属板材实施冲压加工时，经常容易出现裂损或划痕的现象。如何克服金属板材冲压过程出现的这一现象成了目前金属板材冲压技术急需解决的技术问题。
技术实现思路
本专利技术的目的在于提供一种金属板材的冲压方法，它可以解决现有金属板材冲压过程中出现裂损或划痕的问题。为了解决上述技术问题，本专利技术所采用的技术方案是：它包括以下步骤：A．将待处理的金属板材加热至50℃～60℃，然后在其表面涂覆一层涂覆物A；其中，所述涂覆物A是由以下重量份混合制成的：润滑油基础油30份～40份、石油树脂为5份～10份、牛皮膏1份～5份以及硅酸镁0.5份～1份；B．将经过A步骤处理的金属板材预冷至0℃～5℃，然后再在其表面涂覆一层涂覆物B；其中，所述涂覆物B是由以下重量份混合制成的：润滑油基础油30份～40份、石油树脂为5份～10份、粘土1份～5份以及二氧化硅0.5份～1份；C．将经过B步骤处理的金...
【技术保护点】
一种金属板材的冲压方法，其特征在于包括以下步骤：A．将待处理的金属板材加热至50℃～60℃，然后在其表面涂覆一层涂覆物A；其中，所述涂覆物A是由以下重量份混合制成的：润滑油基础油30份～40份、石油树脂为5份～10份、牛皮膏1份～5份以及硅酸镁0.5份～1份；B．将经过A步骤处理的金属板材预冷至0℃～5℃，然后再在其表面涂覆一层涂覆物B；其中，所述涂覆物B是由以下重量份混合制成的：润滑油基础油30份～40份、石油树脂为5份～10份、粘土1份～5份以及二氧化硅0.5份～1份；C．将经过B步骤处理的金属板材放入模具中，按设定的压力启动动压机进行冲压。
【技术特征摘要】
1.一种金属板材的冲压方法，其特征在于包括以下步骤：A．将待处理的金属板材加热至50℃～60℃，然后在其表面涂覆一层涂覆物A；其中，所述涂覆物A是由以下重量份混合制成的：润滑油基础油30份～40份、石油树脂为5份～10份、牛皮膏1份～5份以及硅酸镁0.5份～1份；B．将经过A步...
【专利技术属性】
技术研发人员：梁宇松，
申请(专利权)人：柳州市御朗机械制造有限公司，
类型：发明
国别省市：广西,45