The invention discloses an environment-friendly water-based anti rust agent, which comprises the following components according to the quality of parts: 6 composite acid: 10; film-forming agent: 10 17; 9 triethanolamine: 11; monoethanolamine: 3 5; 7: 5 amide: Deionized water; allowance. The composite acid comprises the following components according to the quality of composition: Eleven carbon dicarboxylic acid: 1 2; sebacic acid: 1 2; 3: 2 boric acid; decanoic acid: 2 Xin 3. The film-forming agent comprises the following components according to the quality of parts: 5: polyethylene glycol 7; glycerol: 5 10. The invention provides an environment-friendly water-based anti rust agent, using compound acid and film-forming agent effective collocation, improve the antirust performance and long-term stability, can effectively improve anti-corrosion products pass rate, excellent characteristics of reducing production cost.
【技术实现步骤摘要】
一种环保型水基防锈剂
本专利技术涉及防锈剂领域，具体涉及一种环保型水基防锈剂。
技术介绍
防锈剂主要适用于机械加工过程中金属加工件、铸件、锻件、烧结件及各种型材等零部件在工序间的短、中期和库存防锈处理。也适用于工业生产企业的各种机械、设备在检修过程中的黑色金属材料，零部件的短、中期防锈处理。水基防锈剂无毒或者毒性很小，没有气味，不会燃烧，使用该类产品的金属工件在进入下一道工序前无需清洗或者仅需要简单清洗，大大简化了处理工序，提高了效率，加上用水取代了有机溶剂，具有环保、防火、对操作人员危害小等优点，是防锈产品的发展方向。传统的水性防锈处理是将亚硝酸钠、重铬酸盐等按照一定浓度溶解于水中组成水性防锈液，其特点是操作简单，适用于金属加工工序间短期防锈，防锈期大约20天左右；但这种防锈剂对操作人员毒性大，环境污染严重。因此，研制出可以长时间防锈的环保型水基防锈剂，不仅对环保事业具有积极影响，还可以进一步推进工业的发展。
技术实现思路
本专利技术所要解决的技术问题是提供一种环保型水基防锈剂，利用复合酸和成膜剂的有效搭配，提高防锈性能和长期稳定性，具有有效提高产品防腐合格率，降低...
【技术保护点】
一种环保型水基防锈剂，其特征在于，由以下组分按质量份组成：复合酸：6‑10份；成膜剂：10‑17份；三乙醇胺：9‑11份；一乙醇胺：3‑5份；酰胺：5‑7份；去离子水：余量。
【技术特征摘要】
1.一种环保型水基防锈剂，其特征在于，由以下组分按质量份组成：复合酸：6-10份；成膜剂：10-17份；三乙醇胺：9-11份；一乙醇胺：3-5份；酰胺：5-7份；去离子水：余量。2.根据权利要求1所述的环保型水基防锈剂，其特征在于，所述复合酸包括十一碳二元酸、癸二酸、硼酸以及辛葵酸。3.根据权利要求2所述的环保型水基防锈剂，其特征在于，所述复合酸由以下组分按质量份组成：十一碳二元酸：1-2份；癸二酸：1-2份；硼酸：2-3份；辛葵酸：2-3份。4.根据...
【专利技术属性】
技术研发人员：卢建波，
申请(专利权)人：上海希勒化学有限公司，
类型：发明
国别省市：上海,31