The invention discloses a preparation method of dust water repellent coatings, first mixing three fluorine methyl propyl silicone, acrylic acid, isooctyl two pentaerythritol, ethylene glycol monobutyl ether and ethyl orthosilicate, get a mixture; and then added to the mixture in a dispersing agent, after mixing with silica, titanium dioxide, get the mixture at the end of two; the curing agent is added in the mixture of 2, mixing by grinding machine, dust water repellent coatings. The preparation method of the dustproof hydrophobic paint provided by the invention has the characteristics of fast drying time, strong adhesive force and good hydrophobic property.
【技术实现步骤摘要】
一种防尘憎水涂料的制备方法
本专利技术属于涂料领域，具体涉及一种防尘憎水涂料的制备方法。
技术介绍
涂料是一种涂敷在固体材料(被保护被装饰对象)表面并能形成牢固附着的连续薄膜的配套性工程材料。目前市场上出现的涂料品种约有一千种以上，其中由化工部颁发的产品型号就有近千种，新发展的型号有数百种，今后，随着高科技术业发展和国防建设的需要，新的涂料品种还将不断出现。防尘涂料即是一种涂层表面不易被其它粘性物质所粘附或粘附后易被除去的特种涂料。目前防尘涂料的研究方法一般分为两种：一是用低表面能氟树脂来充当涂层的成膜物质或在涂料中加入低表面能的含氟添加剂的氟碳涂料；而另一种就是根据荷叶自清洁特性，在涂层构造出具有微纳米结构的表面，再通过低表面能的化学物质对其表面进行化学修饰，得到的疏水或超疏水的涂层。目前玻璃表面使用的防尘涂料由于特定的基体而导致涂料附着性能与硬度不高，且防尘效果也需要加强。建筑防水涂料系由合成高分子材料、沥青、聚合物改性沥青、无机材料等为主体，掺入适量的助剂、改性材料、填充材料等加工制成的溶剂型、水溶型、水乳型或粉末型的防水材料。与防水卷材相比，防水涂料施工简...
【技术保护点】
一种防尘憎水涂料的制备方法，其特征在于，包括以下步骤：步骤1，将以重量份计的甲基三氟丙基硅油5‑10份、丙烯酸异辛酯2‑6份、二季戊四醇3‑8份、乙二醇丁醚10‑20份和正硅酸乙酯3‑8份搅拌混合20‑30分钟，得到混合物一；步骤2，在混合物一中加入分散剂0.5‑1份，混合后加入二氧化硅5‑8份、二氧化钛2‑5份，得到混合物二；步骤3，在混合物二中加入固化剂1‑2份，搅拌混合后通过研磨机研磨后，得到防尘憎水涂料。
【技术特征摘要】
1.一种防尘憎水涂料的制备方法，其特征在于，包括以下步骤：步骤1，将以重量份计的甲基三氟丙基硅油5-10份、丙烯酸异辛酯2-6份、二季戊四醇3-8份、乙二醇丁醚10-20份和正硅酸乙酯3-8份搅拌混合20-30分钟，得到混合物一；步骤2，在混合物一中加入分散剂0.5-1份，混合后加入二氧化硅5-8份、二氧化钛2-5份，得到混合物二；步骤3，在混合物二中加入固化剂1-2份，搅拌混合后通过研磨机研磨后，得到防尘憎水涂料。2.根据权利要求1所述的防尘憎水涂料的制备方法，其特征在于，步骤1中搅拌混合...
【专利技术属性】
技术研发人员：孙海，
申请(专利权)人：江苏达克罗涂装技术有限公司，
类型：发明
国别省市：江苏,32