The invention relates to a method for ultra high temperature vacuum drying rock asphalt powder, using ultra high temperature chimney rock asphalt powder on the dryer for rapid drying, produced in the drying process of water vapor and dust caused by rock asphalt fan, the dryer is always in the negative state during the drying process. The invention uses ultra high temperature hot gas to dry rock asphalt powder, and can prevent the melting, agglomeration and adhesion of the rock asphalt powder when drying, thereby ensuring the quality and efficiency of the drying. At the same time, the dryer steam extraction fan, the dryer in the vacuum state, while reducing the security risks and damage to the equipment, on the other hand dryer under negative pressure so that drying speed is faster.
【技术实现步骤摘要】
一种超高温负压干燥岩沥青粉的方法
本专利技术属于岩沥青加工领域，涉及一种干燥岩沥青粉的方法，具体涉及一种超高温负压干燥岩沥青粉的方法。
技术介绍
岩沥青粉是一种天然沥青改性剂，由天然岩沥青矿料加工而成，用来对道路施工中的沥青混合原料进行改性。经过岩沥青粉改性后的沥青具有更加优越的路用性能，与传统的改性剂相比，大幅提高了道路对车辙、水损害、裂缝、坑槽、拥包的抗性，通过多年来国内外的试验研究和工程实践，越来越受到重视，具有广大的推广和应用前景。但岩沥青粉的加工设备和工艺相对落后，制约了其在道路施工中的大规模应用。在使用岩沥青粉作为改性剂之前，需要对其进行干燥，目前岩沥青粉的干燥工艺仍然是采用对流干燥的方式，将来自燃烧装置的热能以对流方式由热气体传导至湿物料表面，由物料表面传至物料内部，使物料水分充分蒸发。由于与一般的矿石原料相比，岩沥青矿含水量不稳定，含油量高，对热量敏感，在干燥过程中受热容易软化、结块，操作不当容易起火燃烧，还会引起岩沥青老化。因此在干燥岩沥青粉的过程中，国内一般采用低温常压干燥方法，温度一般低于200℃，筒内压力基本与环境压力一致，干燥效率约为75...
【技术保护点】
一种超高温负压干燥岩沥青粉的方法，其特征在于，采用超高温热气流对干燥器内的岩沥青粉进行快速干燥，干燥过程中产生的水蒸气和部分岩沥青粉尘由引风机引出，使干燥器在干燥过程中始终处于负压状态。
【技术特征摘要】
1.一种超高温负压干燥岩沥青粉的方法，其特征在于，采用超高温热气流对干燥器内的岩沥青粉进行快速干燥，干燥过程中产生的水蒸气和部分岩沥青粉尘由引风机引出，使干燥器在干燥过程中始终处于负压状态。2.根据权利要求1所述的超高温负压干燥岩沥青粉的方法，其特征在于，干燥温度为370-420℃。3.根据权利要求1所述的超高温负压干燥岩沥青粉的方法，其特征在于，在干燥过程中，所述干燥器内的压力为0.6-0.8个大气压。4.根据权利要求1所述的超高温负压干燥岩沥青粉的方法，其特征在于，干燥完成的岩沥青粉从干燥器的卸料口排出并收集，所述岩沥青粉从进料到出料的时间为25-30s。5.根据权利要求2所述的超高温负压干燥岩沥青粉的方法，其特征在于，在干燥之前，向干燥器内通入热气流，对干燥器进行预热处理。6.根据权利要求5所述的超高温负压干燥岩沥青粉的方法，...
【专利技术属性】
技术研发人员：龚城，王世友，
申请(专利权)人：北京路优材料技术有限公司，
类型：发明
国别省市：北京,11