The invention discloses a light alloy glasses and its preparation method, preparation of light alloy glasses as raw material: magnesium, titanium, cadmium, nickel, manganese, Dy, the other is aluminum; the light alloy glasses outer metal plating film; the preparation method is as follows: step S1, the quality of percentage of magnesium, titanium, cadmium, nickel, manganese, dysprosium and aluminum in the vacuum casting machine feeding port, and then in the melting device for molten melt; step S2, the solution obtained in step S1 into the mold gate set, and then to the punch will melt into the mold frame; step S3, the solution cooling molding steps S2 glasses in the mold, the light glasses frame; step S4, polishing of the glasses, polishing and coating postprocessing. The preparation process of the invention is simple, and the lightweight alloy glasses frame has low specific gravity, good elasticity and elasticity, and does not irritate the skin.
【技术实现步骤摘要】
一种轻质合金眼镜架及其制备方法
本专利技术涉及眼睛架领域，具体涉及一种轻质合金眼镜架及其制备方法。
技术介绍
目前，市场上眼睛架的材料种类繁多，主要有塑料、树脂材料和金属材料。其中，塑料材料虽然质轻、美观，但是不耐高温，易燃；树脂材料，因其强度高、比重低和抗变性被广泛应用、但其硬度低。目前应用的金属材料主要有：白铜、黄铜、钛合金等；这些合金虽然耐高温、弹性和强度大。但是其比重大，极大的影响佩戴。市场上使用的铝合金镜框虽然比重低，耐热、弹性好，但是硬度低、易氧化、不美观。中国专利CN101724766公开了一种弹性耐磨的眼镜架材料及其制备方法，材料成分主要是Ni，再加入Cu、Zn、W组分。但是该专利比重大、抗变形能力差、制备方法简单。因此，为解决上述问题，急需一种制备工艺简单，比重低、弹韧性好、不刺激皮肤的轻质合金眼镜架。
技术实现思路
本专利技术针对上述问题，提供一种轻质合金眼镜架及其制备方法。本专利技术解决上述问题所采用的技术方案是：一种轻质合金眼镜架，制备轻质合金眼镜架的原料及其质量百分数为：镁8％～15％、钛4％～10％、镉2％～4％、镍1％～2％、锰0.2％～...
【技术保护点】
一种轻质合金眼镜架，其特征在于，制备所述轻质合金眼镜架的原料及其质量百分数为：镁8％～15％、钛4％～10％、镉2％～4％、镍1％～2％、锰0.2％～0.4％、镝0.05％～0.15％、其余为铝；所述轻质合金眼睛架外层镀金属膜。
【技术特征摘要】
1.一种轻质合金眼镜架，其特征在于，制备所述轻质合金眼镜架的原料及其质量百分数为：镁8％～15％、钛4％～10％、镉2％～4％、镍1％～2％、锰0.2％～0.4％、镝0.05％～0.15％、其余为铝；所述轻质合金眼睛架外层镀金属膜。2.根据权利要求1所述的轻质合金眼镜架，其特征在于，所述轻质合金眼镜架的比重为：3.1～3.7。3.根据权利要求1所述的轻质合金眼镜架，其特征在于，所述轻质合金眼镜架的鼻梁叠片为：亚克力。4.根据权利要求1所述的轻质合金眼镜架，其特征在于，所述轻质合金眼镜架的镜腿套有亚克力。5.根据权利要求1所述的轻质合金眼镜架，其特征在于，所述金属膜为：金、银或钛合金。6.一种根据权利要求1～5中任一项所述的轻质合金眼镜架的制备方法，其特征在于，包括以下步骤：步骤S1...