用于催化降解有机污染物的金属有机骨架薄膜及其制备方法技术
Metal organic framework film for catalyzing and degrading organic pollutant and preparation method thereof
The invention discloses a metal organic framework film for catalyzing and degrading organic pollutants and a preparation method thereof. The method comprises the following steps: 1) ZIF 67 nanoparticles dispersed in N, N two dimethylformamide (DMF) solution, adding polyacrylonitrile (PAN), ZIF 67 nanoparticles and stir until pan mixed evenly; 2) in the mixed solution as the spinning solution by electrospinning technique, ZIF films 67 PAN. ZIF 67 PAN film prepared by the invention has good flexibility, has very high catalytic activity, and can solve the long time recycling of metal organic framework materials in solution easy to agglomerate, difficult reuse. The application of organic pollutants in degradation wastewater showed good performance.
【技术实现步骤摘要】
用于催化降解有机污染物的金属有机骨架薄膜及其制备方法
本专利技术属于环境纳米材料领域，具体涉及一种用于催化降解有机污染物的金属有机骨架薄膜及其制备方法。
技术介绍
在城镇化和工业化迅速发展的今天，环境污染已经成为世界的焦点，引起了越来越多人的强烈关注。其中，有机物污染，尤其是有机染料污染，因其会对水体透明度及气体溶解度造成严重影响，此外还有一些染料具备高毒性、致癌性和致突变性，能够通过生物链而累积。因此，寻找一种能够用于处理含有有机染料的工业废水的有效方法，对于缓解我国所面临的严峻的环境污染问题显得尤为重要。近年来基于硫酸根自由基的高级氧化工艺，因其具备较高的氧化电位，具备良好的选择性和高的效率等一系列优点，已经成为一种前景光明的选择。林坤儀课题组（Chemosphere130(2015)66-72）首次报道了通过六水合硝酸钴和2-甲基咪唑（2-MIM）反应制备ZIF-67，并应用于催化硫酸根自由基方面。但是，由于MOF材料本身易团聚，难以回收，影响了其在实际生产当中的应用。
技术实现思路
本专利技术的目的在于提供一种用于催化降解有机污染物的金属有机骨架薄膜及其制备方...
【技术保护点】
一种用于催化降解有机污染物的金属有机骨架薄膜，其特征在于，由如下步骤制备：步骤1，将金属有机骨架材料ZIF‑67在N, N‑二甲基甲酰胺中超声至完全散开，加入与ZIF‑67的质量比为4：(1~3)的聚丙烯腈，搅拌至混合均匀，得到静电纺丝溶液；步骤2，设置纺丝电压的正压为10~12千伏，负压为1~3千伏，推注速率为0.08~0.1 mm/min，将步骤1得到的静电纺丝溶液进行静电纺丝，得到ZIF‑67‑PAN薄膜。
【技术特征摘要】
1.一种用于催化降解有机污染物的金属有机骨架薄膜，其特征在于，由如下步骤制备：步骤1，将金属有机骨架材料ZIF-67在N,N-二甲基甲酰胺中超声至完全散开，加入与ZIF-67的质量比为4：(1~3)的聚丙烯腈，搅拌至混合均匀，得到静电纺丝溶液；步骤2，设置纺丝电压的正压为10~12千伏，负压为1~3千伏，推注速率为0.08~0.1mm/min，将步骤1...
【专利技术属性】
技术研发人员：李健生，王超海，王宏宇，罗瑞，廖志鹏，刘超，孙秀云，沈锦优，韩卫清，王连军，
申请(专利权)人：南京理工大学，
类型：发明
国别省市：江苏,32