The invention discloses a method for preparing foamed glass by using fly ash, the fly ash crushed with methyl methacrylate and acrylic acid, initiator, emulsifier, water mixing, heating reaction, adding SiO2, Fe2O3, K2O, A12O3, CaO, Na2O 0, Li2O 0, MgO, lecithin, filtration, washing filter cake with ethanol, cooling, heating and melting, glass raw materials; the glass raw materials after crushing and foaming agent, fluxing agent, stabilizer mixing, ball milling, in 400 430 DEG C after preheating temperature of foaming, cooling annealing, cooling after making foam glass. The foam glass obtained by the preparation method of the invention has good compressive performance and heat insulation performance.
【技术实现步骤摘要】
一种利用粉煤灰制备泡沫玻璃的方法
本专利技术属于泡沫玻璃
，具体涉及一种利用粉煤灰制备泡沫玻璃的方法。
技术介绍
泡沫玻璃最早是由美国匹兹堡康宁公司专利技术的，是由碎玻璃、发泡剂、改性添加剂和发泡促进剂等，经过细粉碎和均匀混合后，再经过高温熔化，发泡、退火而制成的无机非金属玻璃材料。泡沫玻璃是一种性能优越的绝热(保冷)、吸声、防潮、防火的轻质高强建筑材料和装饰材料，使用温度范围为零下196度到450度，A级不燃与建筑物同寿命，透湿系数几乎为0。虽然其他新型隔热材料层出不穷，但是泡沫玻璃以其永久性、安全性、高可靠性在低热绝缘、防潮工程、吸声等领域占据着越来越重要的地位。它的生产是废弃固体材料再利用，是保护环境并获得丰厚经济利益的范例。目前，我国的粉煤灰利用价值总体较低，多用来生产砖、空心砌块、加气混凝土等，甚至不少地区用来作路基填料。提高粉煤灰的利用价值是国内科技人员的一项紧迫任务。
技术实现思路
本专利技术的目的是提供一种利用粉煤灰制备泡沫玻璃的方法，提高泡沫玻璃的抗压性以及隔热性能。为了实现本专利技术的上述目的，采用以下技术方案：一种利用粉煤灰制备泡沫玻璃的方...
【技术保护点】
一种利用粉煤灰制备泡沫玻璃的方法，其特征在于，包括以下步骤：步骤1，以重量份计，将粉煤灰100份粉碎后与甲基丙烯酸甲酯5‑10份、丙烯酸10‑20份、引发剂3‑7份、水20‑30份、乳化剂1‑3份混合，加热反应，再加入SiO2 1‑3份、Fe2O3 0.8‑2.5份、K2O 0.5‑1.2份、A12O3 0.7‑1.5份、CaO 0.4‑0.9份、Na2O 0.5‑1份、Li2O 0.7‑2.4份、MgO 1‑3份、卵磷脂0.1‑0.5份，抽滤，用乙醇洗涤滤饼，加热熔融、冷却，得到玻璃原料；步骤2，以重量份计，将步骤1所得玻璃原料100份粉碎后与发泡剂10‑15份、助熔剂2...
【技术特征摘要】
1.一种利用粉煤灰制备泡沫玻璃的方法，其特征在于，包括以下步骤：步骤1，以重量份计，将粉煤灰100份粉碎后与甲基丙烯酸甲酯5-10份、丙烯酸10-20份、引发剂3-7份、水20-30份、乳化剂1-3份混合，加热反应，再加入SiO21-3份、Fe2O30.8-2.5份、K2O0.5-1.2份、A12O30.7-1.5份、CaO0.4-0.9份、Na2O0.5-1份、Li2O0.7-2.4份、MgO1-3份、卵磷脂0.1-0.5份，抽滤，用乙醇洗涤滤饼，加热熔融、冷却，得到玻璃原料；步骤2，以重量份计，将步骤1所得玻璃原料100份粉碎后与发泡剂10-15份、助熔剂2-8份、稳定剂1-4份混合，球磨，在400-430℃预热后升温进行发泡，降温退火，冷却后即制得泡沫玻璃。2.根据权利要求1所述的利用粉煤灰制...
【专利技术属性】
技术研发人员：孙祯彬，苏复，
申请(专利权)人：江苏耀兴安全玻璃有限公司，
类型：发明
国别省市：江苏,32