The invention discloses a method for extraction of rare earth rare earth oxide from waste residue, it will waste rare earth, rare earth polishing powder residue by alkali roasting and acid washing after removing impurity, rare earth oxide product obtained by filtration and washing and drying after precipitation, recycling cycle after the filtrate was acidified into alkali roasting, and then by oxalic acid sedimentation and filtration purification, produced by oxidation of rare earth products. The production method of the invention further improves the recovery rate of the rare earth component, further simplifies the production process of rare earth recovery and improves the labor efficiency.
【技术实现步骤摘要】
一种从稀土废渣中提取氧化稀土的方法
本专利技术涉及材料制备
，更具体的说是涉及一种从稀土废渣中提取氧化稀土的方法。
技术介绍
稀土抛光粉因其具有独特的物理和化学性质，被广泛应用于显示屏、光学光电玻璃、饰品、建材、模具及精密仪器的精磨。据统计，2011年，我国稀土抛光粉产量15500t(实物量)，合法稀土矿山矿产品产量8.49万吨(REO)，生产稀土抛光粉实际消耗稀土大约13950吨(REO)占指令性计划的16.43％。稀土抛光粉应用量4800t(REO)比上年增长4.35％。随着稀土抛光粉应用量的增加，形成的稀土抛光粉固体废渣也在不断增加。稀土抛光粉废渣主要是由稀土抛光粉抛光废液沉淀分离的固体渣料。其主要成分是含镧和铈的稀土氧化物、被磨下来的玻璃颗粒、抛光机上的磨皮(有机聚合物)、及废液中人工混入的沉淀剂氯化铝等，这些废渣中的稀土元素很难用简单的方法回收再利用，造成稀土资源的浪费。目前国内外已有稀土抛光粉废渣的回收利用的报道，日本专利JP11319F55及国内专利“失效的稀土抛光粉的再生方法”采用氢氟酸或氟化物去除废渣中的玻璃成分，从而达到回收的目的，不仅工...
【技术保护点】
一种从稀土废渣中提取氧化稀土的方法，其特征在于：它包括以下步骤，(1)将稀土废渣粉碎，得到稀土废渣粉；将稀土废渣粉、氢氧化钠及水混合均匀，后加热焙烧后制成焙烧物；(2)将经过步骤(1)处理后的焙烧物粉碎，加水煮沸20‑30min，然后过滤，将水洗渣与滤液分离；(3)将步骤(2)中的水洗渣稀盐酸酸化至配pH为5‑6，溶液加热煮沸后，以碱溶液调节溶液pH值为6.8‑7，静置分层后，用离心或压滤的方法将固体与溶液分离，固体经烘干得到稀土氧化物成品；步骤(2)中的滤液循环参与到步骤(1)中，代替水与稀土废渣粉、氢氧化钠进行混合；滤液经过2‑3次循环后，停止循环，储存备用；(4)将步...
【技术特征摘要】
1.一种从稀土废渣中提取氧化稀土的方法，其特征在于：它包括以下步骤，(1)将稀土废渣粉碎，得到稀土废渣粉；将稀土废渣粉、氢氧化钠及水混合均匀，后加热焙烧后制成焙烧物；(2)将经过步骤(1)处理后的焙烧物粉碎，加水煮沸20-30min，然后过滤，将水洗渣与滤液分离；(3)将步骤(2)中的水洗渣稀盐酸酸化至配pH为5-6，溶液加热煮沸后，以碱溶液调节溶液pH值为6.8-7，静置分层后，用离心或压滤的方法将固体与溶液分离，固体经烘干得到稀土氧化物成品；步骤(2)中的滤液循环参与到步骤(1)中，代替水与稀土废渣粉、氢氧化钠进行混合；滤液经过2-3次循环后，停止循环，储存备用；(4)将步骤(3)中储存备用的滤液经草酸沉淀，得到草酸稀土，草酸的加...
【专利技术属性】
技术研发人员：肖兴才，车兴玉，
申请(专利权)人：乐山东承新材料有限公司，
类型：发明
国别省市：四川,51
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。