The present invention provides an antiskid pavement material and a preparation method thereof, the liquid and additives were prepared; the solution comprises the following components in parts by weight: methyl methacrylate 1 20; 2 ethylhexyl 1 10; 70 80 acrylic resin; the additive package the method comprises the following components in parts by weight: 0.5 accelerator 0.8; curing agent 1 2; two methyl amino toluene 0.2 0.75; calcium carbonate 0.05 0.2; 0.8 1.5 inorganic filler. And skid resistance, abrasion resistance and impact resistance and other excellent properties attached to the antiskid pavement material and road; curing time is short, the construction of a short time after the vehicle can pass, the work is very strong, good appearance, short curing time.
【技术实现步骤摘要】
一种防滑铺装材料及其制备方法
本专利技术属于地面铺装材料领域，尤其是涉及一种防滑铺装材料及其制备方法。
技术介绍
聚甲基丙烯酸甲酯(MMA树脂)是一种广泛用于土木建筑及医疗、电子产品等领域的环保型材料,因其反应速度快而在施工现场配合使用。以丙烯酸或甲基丙烯酸合成的聚合物，拥有碳双重结构(C＝C)，是一种具有超强的耐久性，物理性能和防水性能的树脂。MMA树脂因其优秀的物理属性和快速固化、耐久性能、环保功能等特点，不仅适用于地板防滑铺装材料，还适用于紧急道路抢修、道路铺装、桥面防水、厨房地板等多个领域，而且其使用范围正在替代水泥浆料、环氧树脂、聚氨酯等原有的地板材料。防滑铺装材料，是一种特殊的有机材料，可以辅助地增强道路的防滑性。道路防滑用铺装材料不仅在交叉路、急转弯路和倾斜路上可以使用，而且在学校前、横断步道的前方道路等交通事故多发地区设置后，可以防止车辆打滑，保持车辆间的车距，从而将交通事故防患于未然。现有的道路防滑铺装材料主要有环氧系树脂等有机溶剂型道路铺装材料、水溶性道路铺装材料和热熔型道路铺装材料，其中，环氧系树脂的耐碱性和附着性良好，但耐候性略差，作业时间...
【技术保护点】
一种防滑铺装材料，其特征在于：所述铺装材料由原液和添加剂制备而得；所述原液包括如下重量份数的组分：甲基丙烯酸甲酯1‑20份；2‑乙基己酯1‑10份；亚克力树脂70‑80份；所述添加剂包括如下重量份数的组分：促进剂0.5‑0.8份；固化剂1‑2份；对二甲氨基甲苯0.2‑0.75份；碳酸钙0.05‑0.2份；无机填料0.8‑1.5份。
【技术特征摘要】
1.一种防滑铺装材料，其特征在于：所述铺装材料由原液和添加剂制备而得；所述原液包括如下重量份数的组分：甲基丙烯酸甲酯1-20份；2-乙基己酯1-10份；亚克力树脂70-80份；所述添加剂包括如下重量份数的组分：促进剂0.5-0.8份；固化剂1-2份；对二甲氨基甲苯0.2-0.75份；碳酸钙0.05-0.2份；无机填料0.8-1.5份。2.根据权利要求1所述的防滑铺装材料，其特征在于：所述促进剂为N·N-二乙基苯胺、环烷酸钴、异辛酸钴、萘酸钴一种或两种以上的混合。3.根据权利要求1所述的防滑铺装材料，其特征在于：所述促进剂为异辛酸钴。4.根据权利要求1所述的防滑铺装材料，其特征在于：所述固化剂为过氧化苯甲酰、过氧化二异丙苯、过氧化叔丁酯、过氧化环己酮、过氧化甲乙酮中的一种或两种以上的混合。5.根据权利要求1所述的防滑铺装材料，其特...
【专利技术属性】
技术研发人员：孙长宏，孙庆兰，
申请(专利权)人：天津佰思特新材料科技有限公司，
类型：发明
国别省市：天津,12