一种钛合金激光焊接保护方法技术
Laser welding protection method for titanium alloy
A titanium alloy laser welding protection method, which is characterized in that the process of laser welding protection with two sets of air, in which a group of air is helium and through a protective cover to acute placed conveying the welding area to protect molten pool, gas flow rate of Q1 is 8 to 16 L/min, another group of gas argon is low the ionization energy and the level of protection is placed cover transported to the rear of weld pool and weld metal for cooling, gas flow rate of Q2 is 12 to 20 L/min, and the two groups of air independent settings, gas flow Q2, gas flow Q1. The invention adopts two different groups of air flow, can provide effective protection of gas laser welding for titanium alloy parts, can obtain high quality welding joint of titanium alloy, and can be in 1 ~ 12mm thick plate titanium alloy laser welding for effective protection.
【技术实现步骤摘要】
一种钛合金激光焊接保护方法
本专利技术属于材料激光加工
，具体是涉及一种钛合金激光焊接保护方法。
技术介绍
钛合金具有优良的性能，在工业领域得到了广泛的应用，尤其在航空航天领域。随着钛合金应用范围扩大，其自身的焊接加工问题也日益突出。由于钛元素活泼性高，焊接过程中易吸氢、吸氧、吸氮导致其塑性下降。因此，在钛合金的激光焊接过程中，由于焊接速度较快，凝固后的焊缝温度还较高，需要同时对熔池和以凝固的焊缝进行保护。钛合金激光焊接的气体保护方法目前主要有两种：一种是真空室条件焊接，该种方法虽能很好保证焊接效果，但是其成本极高，不利于工业化推广；另一种是气体保护，气体保护方法包括同轴气体保护、侧吹气体保护。公开号为CN105728940A的专利技术专利申请，公开了一种激光焊接同轴气体保护方法，该方法一般采用氦气或者氩气或者氦气氩气混合气。该方法的缺点是只能对熔池进行保护，未能很好地保护已凝固的焊缝金属，导致焊缝氧化，呈现黑色或者黄色表面，影响力学性能。公开号为CN105171236A的专利技术专利申请，公开了一种激光焊接单管侧吹气体保护方法，该方法存在跟同轴气体保护一样...
【技术保护点】
一种钛合金激光焊接保护方法，其特征在于：采用两组气流对激光焊接过程进行保护，其中一组气流为氦气并通过呈锐角放置的保护罩输送到焊接区域用来保护熔池，气体流量Q1为8～16 L/min，另一组气流为低电离能的氩气并通过呈水平放置的保护罩输送到熔池尾部和焊缝用于冷却金属，气体流量Q2为12～20 L/min，且两组气流相互独立设置，气体流量Q2＞气体流量Q1。
【技术特征摘要】
1.一种钛合金激光焊接保护方法，其特征在于：采用两组气流对激光焊接过程进行保护，其中一组气流为氦气并通过呈锐角放置的保护罩输送到焊接区域用来保护熔池，气体流量Q1为8～16L/min，另一组气流为低电离能的氩气并通过呈水平放置的保护罩输送到熔池尾部和焊缝用于冷却金属，气体流量Q2为12～20L/min，且两组...