The invention discloses a method for preparing a titanium alloy, which comprises the following steps: cleaning steps, a titanium alloy; step of plating B, titanium alloy, the chemical plating Ni P Si C composite electroless plating, cleaning is good in titanium alloy composite plating liquid for chemical plating, chemical plating conditions for plating temperature is 80 DEG C for 6.5 PH 90, 7.5, stirring speed 10 20 rpm, the bath load is 0.8 1.5dm2/L, plating time 0.5 1 hours. Compared with the prior art, the selection of stabilizers, the phosphorus content of electroless plating of titanium alloy is 3.33 3.35%, hardness is 780 820HV, the friction coefficient is 0.6 0.7, the stability of the bath, the prepared bath life of 1 1.5 hours.
【技术实现步骤摘要】
本专利技术属于合金的制备方法，特别属于钛合金的制备方法。
技术介绍
钛合金是一种新型的结构材料，具有质量轻、比强度高的特点，钛合金中的Ti6Al4V(TC4)是航空工业的主体材料，但其存在表面容易氧化，硬度小于600HV的特点。
技术实现思路
本专利技术所要解决的技术问题是提供一种硬度大于750HV的钛合金的制备方法。本专利技术解决技术问题的技术方案为：一种航空钛合金的制备方法，包括以下步骤：a、钛合金的清洗步骤；b、钛合金的化学镀步骤。所述的化学镀为Ni-P-Si-C复合化学镀，即将清洗好的钛合金放入复合镀液中进行化学镀，化学镀的条件为：施镀温度为80-90℃，PH为6.5-7.5，搅拌速度为10-20转/分，镀液装载量为0.8-1.5dm2/L，施镀时间0.5-1小时。所述的复合镀液中，每升溶液中含有以下物质：所述的氨水用来调节化学镀过程中镀液的PH值。所述的钛合金的清洗步骤依次包括以下步骤：砂纸打磨步骤、除油步骤、酸洗步骤、活化步骤。所述的除油步骤为用超声波清洗砂纸打磨好的钛合金，超声波频率为50-70KHz,清洗10-30分钟。所述的钛合金为Ti6Al4V(TC4)。本专利技术与现有技术相比，通过选择2-氨基-5-巯基-1,3,4-噻二唑、D-(+)-二苯甲酰酒石酸一水物作为稳定剂，化学镀出的钛合金的含磷量为3.33-3.35％，硬度为780-820HV，摩擦系数为0.6-0.7，镀液的稳定性好，配制好的镀液的寿命为1-1.5小时。具体实施方式下面结合实施例对本专利技术作详细的说明。实施例1：一种航空钛合金的制备方法，包括以下步骤：a、钛合金的清洗步...
【技术保护点】
一种航空钛合金的制备方法，包括以下步骤：a、钛合金的清洗步骤；b、钛合金的化学镀步骤，其特征在于：所述的化学镀为Ni‑P‑Si‑C复合化学镀，即将清洗好的钛合金放入复合镀液中进行化学镀，化学镀的条件为：施镀温度为80‑90℃，PH为6.5‑7.5，搅拌速度为10‑20转/分，镀液装载量为0.8‑1.5dm2/L，施镀时间0.5‑1小时。
【技术特征摘要】
1.一种航空钛合金的制备方法，包括以下步骤：a、钛合金的清洗步骤；b、钛合金的化学镀步骤，其特征在于：所述的化学镀为Ni-P-Si-C复合化学镀，即将清洗好的钛合金放入复合镀液中进行化学镀，化学镀的条件为：施镀温度为80-90℃，PH为6.5-7.5，搅拌速度为10-20转/分，镀液装载量为0.8-1.5dm2/L，施镀时间0.5-1小时。2.根据权利要求1所述的一种航空钛合金的制备方法，其特征在于：所述的复合镀液中，每...
【专利技术属性】
技术研发人员：吴长应，
申请(专利权)人：芜湖扬展新材料科技服务有限公司，
类型：发明
国别省市：安徽;34