制备还原氧化石墨烯/纳米四氧化三铁复合磁性吸附剂的方法技术
Method for preparing reduced oxidation graphene oxide / nano iron oxide composite magnetic adsorbent
The invention discloses a method for preparing graphene / Fe3O4 composite magnetic adsorbents, the scheme is (1) configuration mesoporouscarbons and uniformly mixed reactant mixed solution, the reaction system comprises a water / glycol solvent, two yuan, six graphene oxide, ferric chloride sodium citrate and sodium acetate; (2) preparation of composite magnetic adsorbents by water / glycol co thermal method. The invention improves the traditional solvothermal method, and uses the water and ethylene glycol two element solvent thermal method to make the prepared rGO/Fe3O4 have good magnetic response capability.
【技术实现步骤摘要】
制备还原氧化石墨烯/纳米四氧化三铁复合磁性吸附剂的方法
本专利技术属于吸附剂材料制备领域，具体是制备还原氧化石墨烯/纳米四氧化三铁复合磁性吸附剂的方法。
技术介绍
石墨烯是一种新颖的碳材料，具有特殊的二维结构，蕴含丰富而新奇的物理现象，表现出许多优异的性质，其中包括电学，光学，热学及力学性质。随着对石墨烯的研究越来越深入，科学家们认为，石墨烯有望彻底变革材料科学领域。石墨烯的性质为其广泛的应用范围奠定了基础，有望在高性能纳米电子器件、复合材料、场发射材料、气体传感器及能量存储等领域获得广泛应用。还原氧化石墨烯（rGO）是石墨烯主要的衍生物之一，指通过化学或热处理等方法不完全去除氧化石墨烯中的含氧官能团后得到的一种二维碳材料。rGO的物理化学性质介于石墨烯和氧化石墨烯之间，但是在结构和功能上显示出许多独特的优势。将其作为催化载体时可显示出比石墨烯和GO更大的比表面积和电化学活性（参看王泽高，石墨烯薄膜与还原氧化石墨烯粉末的可控制备及掺杂效应研究，电子科技大学博士学位论文，2014）。最新研究发现，rGO具有优异的吸附性能，是一种很有潜力的吸附剂材料（参看DingWa...
【技术保护点】
一种制备还原氧化石墨烯/纳米四氧化三铁复合磁性吸附剂的方法，其特征在于包括以下步骤：（1）配置反应物体系并混合均匀得到反应物混合溶液，该反应物体系包括有水/乙二醇二元溶剂、氧化石墨烯、六水合氯化铁、柠檬酸钠和乙酸钠，其中，水和乙二醇添加体积比为1/5，氧化石墨烯与水/乙二醇二元溶剂的添加比为3 mg/mL，六水合氯化铁的质量是氧化石墨烯质量的2‑5倍，六水合氯化铁、柠檬酸钠、乙酸钠三者质量比为1/0.4/3；将反应物混合溶液转移至反应釜中；（2）采用水/乙二醇共热法制备复合磁性吸附剂，将反应釜置于马弗炉中，反应温度为180‑200℃，反应时间为8‑12小时，将反应产物充分清...
【技术特征摘要】
1.一种制备还原氧化石墨烯/纳米四氧化三铁复合磁性吸附剂的方法，其特征在于包括以下步骤：（1）配置反应物体系并混合均匀得到反应物混合溶液，该反应物体系包括有水/乙二醇二元溶剂、氧化石墨烯、六水合氯化铁、柠檬酸钠和乙酸钠，其中，水和乙二醇添加体积比为1/5，氧化石墨烯与水/乙二醇二元溶剂的添加比为3mg/mL，六水合氯化铁的质量是氧化石墨烯质量的2-5倍，六水合氯化铁、柠檬酸钠、乙酸钠三者质量比为1/0.4/3；将反应物混合溶液转移至反应釜中；（2）采用水/乙二醇共热法制备复合磁性吸...