The invention relates to a high water flux flat ceramic membrane separating film layer and a preparation method thereof. Including the short cut fiber, mineral aggregate, deionized water, dispersing agent and stabilizer; the amount of material added by weight for short fiber 0~20%, aggregate 80~100%, both solid; deionized water is added to the total solid 0~50%, suspending agent is added to the solid 0~5% of the total amount of dispersant for solid the total amount of 0~3%. The invention provides a separation layer of high water flux of ceramic membrane, which can effectively increase the existing flat ceramic membrane separation membrane water flux, and the sol gel separation layer of long cycle and high cost, and great harm to the problem of drying shrinkage film.
【技术实现步骤摘要】
高水通量平板陶瓷膜分离膜层及其制备方法
本专利技术属于陶瓷膜
，具体涉及一种高水通量平板陶瓷膜分离膜层及其制备方法。
技术介绍
分离膜是涂覆在平板支撑体外层的过滤膜层，能赋予平板陶瓷膜更高的过滤精度和清洗再生性能。目前应用的陶瓷膜分离层采用颗粒堆积法制成，低温烧结而成。膜层孔道主要取决于颗粒堆积，在保证膜层强度的前提下，膜层孔径和气孔率较低，水通量较小。在膜层中添加短切纤维后，纤维之间相互桥接形成大量孔道，有效增加了膜层的水通量，降低膜层阻力。采用溶胶凝胶法制备分离膜层，理论上可以将膜层孔径控制在纳米级别，但是溶胶凝胶法的制备周期较长、工序繁杂、成本较高，并且膜层干燥后收缩较大，容易产生裂纹等缺陷，制备过程中可能会产生对人体有害的气体等物质，不能被大规模推广应用。
技术实现思路
本专利技术针对上述缺陷，目的在于提供一种性能优异的高水通量平板陶瓷膜分离膜层及其制备方法。为此本专利技术采用的技术方案是：本专利技术包括短切矿物纤维、骨料、去离子水、分散剂和稳定剂；各物料加入的量按重量份为：短切纤维0~20%，骨料80~100%，两者为固体；去离子水加入量为固体总量的0...
【技术保护点】
高水通量平板陶瓷膜分离膜层，其特征在于，包括短切矿物纤维、骨料、去离子水、分散剂和稳定剂；各物料加入的量按重量份为：短切纤维0~20%，骨料80~100%，两者为固体；去离子水加入量为固体总量的0~50%，悬浮剂加入量为固体总量的0~5%，分散剂加入量为固体总量的0~3%。
【技术特征摘要】
1.高水通量平板陶瓷膜分离膜层，其特征在于，包括短切矿物纤维、骨料、去离子水、分散剂和稳定剂；各物料加入的量按重量份为：短切纤维0~20%，骨料80~100%，两者为固体；去离子水加入量为固体总量的0~50%，悬浮剂加入量为固体总量的0~5%，分散剂加入量为固体总量的0~3%。2.根据权利要求1所述的高水通量平板陶瓷膜分离膜层，其特征在于，所述短切矿物纤维为氧化铝纤维、氧化锆纤维、多晶莫来石纤维中的一种或多种，纤维直径为2~8μm，长径比为1~20。3.根据权利要求1所述的高水通量平板陶瓷膜分离膜层，其特征在于，所述骨料粒度D50=0~30μm，为氧化铝、氧化钛、氧化锆中的一种或几种。4.根据权...
【专利技术属性】
技术研发人员：张恒网，张久美，华志高，赵世凯，薛友祥，
申请(专利权)人：江苏新时高温材料股份有限公司，山东工业陶瓷研究设计院有限公司，
类型：发明
国别省市：江苏,32