The invention provides an artificial joint material, which is divided into three parts: a joint friction contact surface, a joint body and a joint surface contacting with the human body, wherein the three part is made of materials of different components. Among them, the joint friction contact surface is composed of composite ceramic particles and titanium alloy, titanium alloy joint consists of a joint contact with the human body surface is composed of titanium alloy and biodegradable magnesium alloy composition. The use of composite materials of ceramic particles and titanium alloy forming joint friction contact surface and improve the wear properties of artificial joint, through the use of titanium alloy and biodegradable magnesium alloy is formed in contact with the human body surface improves the stability of interface between prosthesis and host bone.
【技术实现步骤摘要】
一种人工关节材料
本专利技术涉及一种人工关节材料，具体涉及一种成分梯度复合人工关节材料，用于提高人工关节与宿主骨组织之间的生物固定以及人工关节的使用寿命，属于医用材料
技术介绍
人工关节置换术是目前治疗骨关节炎等疾病最有效的手段,人工关节在体内服役时间长(10年以上，甚至可能达30年以上)，服役过程中头-臼结构相对摩擦运动可达数千万次，摩擦导致的磨损不仅仅会使头-臼结构尺寸发生改变，最主要的危害是磨损过程中产生各种磨屑会导致炎症反应及假体失效。目前，人工关节置换术采用的关节主要为金属材质的关节，其耐磨损特性尚有明显不足。而陶瓷材料具有高硬度、良好的耐磨损特性以及生物相容性。为了减少磨屑的产生，研究者开发出了陶瓷-陶瓷(COC)类型摩擦配副的人工关节，已经被成功应用于临床。但是，由于陶瓷材料韧性低，目前临床应用的陶瓷-陶瓷(COC)类型摩擦配副的人工关节，存在着脆性断裂和摩擦噪声大等缺点，这使得陶瓷关节在服役过程中存在较大的安全隐患，会给患者的生活质量造成较大影响。另外，人体内植入物与宿主骨之间的界面结合是维持内植入物的初期和长期稳定的关键因素，增加骨-植...
【技术保护点】
一种人工关节材料，分为关节摩擦接触表面部分、关节主体部分和关节与人体接触表面部分三部分，其特征在于：关节摩擦接触表面部分由陶瓷颗粒与钛合金的复合材料构成，关节主体部分由钛合金构成，关节与人体接触表面部分由钛合金和可降解镁合金构成。
【技术特征摘要】
1.一种人工关节材料，分为关节摩擦接触表面部分、关节主体部分和关节与人体接触表面部分三部分，其特征在于：关节摩擦接触表面部分由陶瓷颗粒与钛合金的复合材料构成，关节主体部分由钛合金构成，关节与人体接触表面部分由钛合金和可降解镁合金构成。2.如权利要求1所述的人工关节材料，其中在关节摩擦接触表面至其深度1mm的范围内陶瓷颗粒的体积比为80-95%，且距离关节摩擦接触表面1.5mm处陶瓷颗粒的体积比降至30%以下。3.如权利要求1所述的人工关节材料，其中在关节与人体接触表面部分，可降解镁合金呈梯度分布；关节与人体接触表面处可降解镁合金的体积浓度为30-80%，距离关节与人体接触表面最远处，可降解镁合金的体积浓度降至10-30%。4.如权利要求3所述的人工关节材料，其中可降解镁合金出现...
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。