一种清水混凝土用表面处理剂制造技术

本发明专利技术属于建筑材料领域，公开了一种清水混凝土用表面处理剂，由以下重量百分比的物质组成：润湿分散剂2％‑5％、膨润土3％‑5％、氯化铝8％‑12％、纳米碳酸钙2％‑3％、磷酸铝3％‑5％、盐酸0.5％‑1％、白糖0.1％‑0.5％、有机硅消泡剂0.001％‑0.005％、余量为水。本发明专利技术产品使用方便，涂刷于清水混凝土表面即可有效填充混凝土表层孔洞，密封固化混凝土表层，防止受到环境中化学物质的侵蚀，延长清水混凝土的使用寿命。

Surface treating agent for fair faced concrete

The invention belongs to the field of building materials, and discloses a concrete surface treatment agent, consisting of the following weight percentage: 2% material wetting dispersant 5%, bentonite 3% 5%, 12%, 8% aluminum chloride nanometer calcium carbonate 2% 3%, 3% aluminum phosphate 5%, 1%, 0.5% hydrochloride 0.5%, sugar 0.1% defoaming agent 0.001% 0.005%, the balance of water. The product of the invention has the advantages of convenient use, brushing on the surface of concrete can be effectively filled with concrete surface holes, seal curing of concrete surface, to prevent the erosion of chemical substances in the environment, prolong the service life of concrete.

【技术实现步骤摘要】
一种清水混凝土用表面处理剂
本专利技术属于建筑材料领域，具体涉及一种清水混凝土用表面处理剂。
技术介绍
混凝土是当代使用量最大的人造材料，具有原料丰富、价格低廉、生产工艺简单等特点。清水混凝土是一次性浇筑成型并不做任何外部抹灰等装饰的混凝土，目前随着人们环保意识的不断提高，清水混凝土技术被越来越多的应用到工程中。但混凝土本质上是一种非均质的多孔材料，水泥水化过程中多余的水分蒸发后会留下毛细孔，水泥和骨料在重力作用下会产生不同的沉降孔，水化产物硅酸钙凝胶本身含有凝胶孔等。清水混凝土因为外部没有抹灰等工序，表面直接裸露于空气中，环境中的水、二氧化碳、二氧化硫等可通过混凝土表面的孔洞进入混凝土内部，造成侵蚀破坏，严重影响其使用寿命。
技术实现思路
本专利技术针对上述问题，提供一种清水混凝土用表面处理剂，实现对混凝土表层毛细孔的封堵，使混凝土表面结构更加密实，防止水和其它侵蚀介质的进入。为达到上述目的，本专利技术采用以下技术方案。一种清水混凝土用表面处理剂，由以下重量百分比的物质组成：润湿分散剂：2％-5％膨润土：3％-5％氯化铝：8％-12％纳米碳酸钙：2％-3％磷酸铝：3％-5％盐酸：0.5本文档来自技高网...

【技术保护点】
一种清水混凝土用表面处理剂，其特征在于，由以下重量百分比的物质组成：润湿分散剂2％‑5％、膨润土3％‑5％、氯化铝8％‑12％、纳米碳酸钙2％‑3％、磷酸铝3％‑5％、盐酸0.5％‑1％、白糖0.1％‑0.5％、有机硅消泡剂0.001％‑0.005％、余量为水。

【技术特征摘要】
1.一种清水混凝土用表面处理剂，其特征在于，由以下重量百分比的物质组成：润湿分散剂2％-5％、膨润土3％-5％、氯化铝8％-12％、纳米碳酸钙2％-3％、磷酸铝3％-5％、盐酸0.5％-1％、白糖0.1％-0.5％、有机硅消泡剂0.001％-0.005％、余量为水。2.根据权利要求1所述的清水混凝土用表面处理剂，其特征在于，所述润湿分散剂由聚丙烯酸钠和烷基酚聚氧乙烯醚非离子表面活性剂组成。3.根据权利要求2所述的清水混凝土用表面处理剂，其特征在于，所述聚丙烯酸钠相对分子质量在1000-5000之间。4.根据权利要求2所述的清水混凝土用表...

【专利技术属性】
技术研发人员：朱社凤，邓颖，周妍蕾，
申请(专利权)人：湖南七纬科技有限公司，
类型：发明
国别省市：湖南,43