一种四水合仲钼酸铵的制备方法技术

本发明专利技术提供了一种四水合仲钼酸铵的制备方法：将钼源和铵源在水中进行复分解反应，得到四水合仲钼酸铵。本发明专利技术以四钼酸铵和/或钼酸作为钼源，以氨水、碳酸氢铵和碳酸铵中的一种或几种作为铵源，无需添加大量的溶剂和水，环保且节约。由实施例的结果可知，本申请提供的制备方法能够成功地得到四水合仲钼酸铵，且其纯度均＞99％。

Method for preparing four hydrated ammonium molybdate

The present invention provides a method for preparing four hydrated ammonium molybdate: the four source of ammonium molybdate is obtained by double decomposition reaction of molybdenum source and ammonium source in water. The present invention uses four ammonium molybdate and / or molybdate as molybdenum source, and uses one or several of ammonia water, ammonium hydrogen carbonate and ammonium carbonate as ammonium source. Without adding a large amount of solvent and water, it is environment-friendly and economical. As a result of the embodiment, the preparation method provided by the present invention can successfully obtain four hydrated ammonium molybdate, and the purity is 99%.

【技术实现步骤摘要】
一种四水合仲钼酸铵的制备方法
本专利技术涉及钼酸铵
，尤其涉及一种四水合仲钼酸铵的制备方法。
技术介绍
四水合仲钼酸铵是一种常用的钼酸铵，分子式是(NH4)6Mo7O24·4H2O。目前，四水合仲钼酸铵被广泛地用于染料、颜料、催化剂、防火剂、微量元素肥料、陶瓷色料及合成其它化合物的原料。目前，现有技术中生产四水合仲钼酸铵的方法普遍都需要在水溶液中进行反应，经过酸沉、氨溶、蒸发结晶等一系列工序得到目标产品。然而，大量水的使用不仅会造成水资源的短缺，生产结束后含氨废水无法直接外排，只能蒸发结晶，造成较高的能量消耗；而且四水合仲钼酸铵产品纯度控制困难，杂质极容易混入其中。
技术实现思路
本专利技术的目的在于提供一种在不添加大量水的情况下制备四水合仲钼酸铵的方法，本专利技术提供的方法流程短、能耗低、污染低、成本低，且操作方便。为了实现上述专利技术目的，本专利技术提供以下技术方案：本专利技术提供了一种四水合仲钼酸铵的制备方法，包含如下步骤：将钼源和铵源在水中进行复分解反应，得到四水合仲钼酸铵；所述钼源为四钼酸铵和/或钼酸；所述铵源为氨水、碳酸氢铵和碳酸铵中的一种或几种；所述钼源、铵源和水的摩本文档来自技高网...

【技术保护点】
一种四水合仲钼酸铵的制备方法，包含如下步骤：将钼源和铵源在水中进行复分解反应，得到四水合仲钼酸铵；所述钼源为四钼酸铵和/或钼酸；所述铵源为氨水、碳酸氢铵和碳酸铵中的一种或几种；所述钼源、铵源和水的摩尔比为(6～8):(2～11):(0～17)。

【技术特征摘要】
1.一种四水合仲钼酸铵的制备方法，包含如下步骤：将钼源和铵源在水中进行复分解反应，得到四水合仲钼酸铵；所述钼源为四钼酸铵和/或钼酸；所述铵源为氨水、碳酸氢铵和碳酸铵中的一种或几种；所述钼源、铵源和水的摩尔比为(6～8):(2～11):(0～17)。2.根据权利要求1所述的制备方法，其特征在于，所述四钼酸铵、碳酸氢铵和水的摩尔比为7:(9～11):(10～12)。3.根据权利要求1所述的制备方法，其特征在于，所述四钼酸铵、碳酸铵和水的摩尔比为7:(4～6):(15～17)。4.根据权利要求1所述的制备方法，其特征在于，所述四钼酸铵、氨水中NH3·H2O和...

【专利技术属性】
技术研发人员：李小斌，杨利群，周秋生，彭志宏，刘桂华，齐天贵，
申请(专利权)人：中南大学，
类型：发明
国别省市：湖南,43