The invention provides a holographic positioning transfer film production method, including a photoresist plate engraved on the holographic patterns of spray silver, electroforming work forms the security work version, on the PET film coated with resin solution of toner layer formation, holographic anti-counterfeiting work on pattern molded into the PET film layer, after vacuum coating in the way of layer plated with a thin layer of metal aluminum, the PET film cutting and packing. The positioning transfer film produced by the invention not only has exquisite patterns, but also has high anti-counterfeiting degree. The color layer has good hardness and good adhesion to the aluminized layer, and no color aluminum delamination occurs during the heat transfer process. The thickness of the lithographic offset plate after spraying silver is uniform and the strength is high, and the yield of the lithographic offset plate is greatly improved, thereby improving the quality of the anti-counterfeit work plate and the transfer film.
【技术实现步骤摘要】
一种全息定位转移膜生产方法
本专利技术属于包装防伪
，涉及一种全息定位转移膜生产方法。
技术介绍
伴随着现代科技的高度发展，假冒伪劣产品也不断地改头换面，渗透到各个领域，无时无刻不在侵害者生产者的正当利益，侵害消费者的权利，因此，防伪打架已成为社会普遍关注的问题。随着国民经济的提高及印刷包装业的发展，人们对产品包装的要求不仅仅是高档、精美、环保、富有个性化，同时也希望通过产品的包装能够辨别产品的真伪。因此，具有防伪功能的彩虹全息模压防伪标识在包装产品的印后加工中得到越来越广泛的应用，并且由于其华贵精美的外观而受到广大消费者的青睐，在烟标、药品、化妆品、酒等高档包装都有广泛的应用。但传统彩虹模压全息防伪标识其一成不变的外观和单一的防伪手段，由于各厂家之间互相模仿以及非法伪造而使其防伪力度大大削弱。
技术实现思路
为解决现有技术存在的问题，本专利技术提供一种全息定位转移膜生产方法，该方法生产的转移膜不仅图案精美、亮度好、图像清晰，并且防伪程度高，色层具有较好的硬度、与镀铝层具有很好的附着力性能，在热转移过程中不会发生色铝分层现象。本专利技术提供的全息定位转移膜生产方...
【技术保护点】
一种全息定位转移膜生产方法，其特征在于，包括以下步骤：(1)利用光刻机将设计好的全息图案刻制在光刻胶版上，再对光刻胶版进行喷银作业，再对光刻胶版电铸形成单枚镍版，电铸形成的镍层厚度大约为50‑100um；利用拼板机将单枚镍版拼成符合要求的大版，对大版电铸形成防伪工作版，该防伪工作版的厚度为0.4‑0.5mm，防伪工作版的厚度偏差小于13um；(2)将PET薄膜卷装在涂布机上，即将PET薄膜卷安装在涂布机的放卷轴上，并使PET薄膜卷的端部从压印辊与网辊之间穿过后安装在收卷辊上；利用酒精和水稀释离型剂，并将稀释好的离型剂倒入涂布机的涂布槽中搅拌均匀，随后开启涂布机在PET薄膜上...
【技术特征摘要】
1.一种全息定位转移膜生产方法，其特征在于，包括以下步骤：(1)利用光刻机将设计好的全息图案刻制在光刻胶版上，再对光刻胶版进行喷银作业，再对光刻胶版电铸形成单枚镍版，电铸形成的镍层厚度大约为50-100um；利用拼板机将单枚镍版拼成符合要求的大版，对大版电铸形成防伪工作版，该防伪工作版的厚度为0.4-0.5mm，防伪工作版的厚度偏差小于13um；(2)将PET薄膜卷装在涂布机上，即将PET薄膜卷安装在涂布机的放卷轴上，并使PET薄膜卷的端部从压印辊与网辊之间穿过后安装在收卷辊上；利用酒精和水稀释离型剂，并将稀释好的离型剂倒入涂布机的涂布槽中搅拌均匀，随后开启涂布机在PET薄膜上涂布离型剂，涂布有离型剂的PET薄膜在收卷过程中从烘箱中穿过，使离型剂在PET薄膜上固化形成离型层；其中网辊采用250目，烘箱烘干温度范围为80-130℃，收卷辊的转速为100m/min，离型剂湿涂量为2.0-2.5g/m2，离型剂固含量为1.0％，涂布厚度为3um左右；(3)对PET薄膜进行涂布加工：将PET薄膜卷装在涂布机上，即，将PET薄膜卷安装在涂布机的放卷轴上，并使PET薄膜卷的端部从压印辊与网辊之间穿过后安装在收卷辊上；将配置好的掺有色粉的树脂溶液倒入涂布机的涂布槽中并搅拌均匀，随后开启涂布机在PET薄膜上涂布色层，涂布有树脂溶液的PET薄膜在收卷过程中从烘箱中穿过，使树脂溶液在PET薄膜上固化形成色层；其中网辊采用200目，烘箱烘干温度范围为85-150℃，收卷辊的转速为100m/min，树脂溶液粘度为16-18S，树脂溶液固含量为22％，湿涂量为5.5-6.0g/m2，烘干后色层上的树脂的干量为1.1-1.2g/m2；所述树脂溶液的组份配比为：醇酸树脂100g、多异氰酸酯固化剂18g、硝基纤维素溶液10g、色粉12g、消泡剂0.4g、流平剂0.4g、润湿分散助剂0.4g、催干剂0.8g、乙酸乙酯130g、乙酸丁酯64g等，其中，硝基纤维素溶液的固含量为10％；(4)将防伪工作版上的全息图案模压到PET薄膜上：将防伪工作版贴在高速模压机的版辊上，将版辊加热至160-180℃，以40kg/cm2左右的压力将版辊上的防伪工作版压在PET薄膜上，使得防伪工作版上的全息图案印在PET薄膜的色层上，形成信息层，其中版辊的硬度为HS97-HS99；(5)将模压后的PET薄膜送入真空镀铝机中，在真空状态下在信息层上镀铝，形成均匀的镀铝层，镀铝层厚度为镀铝机转速为400-500m/min；(6)根据规格要求对PET薄膜进行分切、包装。2.如权利要求1所述的全息定位转移膜生产方法，其特征在于，所述树脂溶液的组份配比为：羟基丙烯酸树脂100g、多异...
【专利技术属性】
技术研发人员：廖香权，杜国栋，
申请(专利权)人：江苏兴广包装科技有限公司，
类型：发明
国别省市：江苏,32
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。