The invention discloses a method for preparing lipophilic modified graphite phase carbon nitride. The preparation method comprises the following steps: graphite carbon nitride and sixteen alkyl three methyl bromide or oleic acid mixture added to acetic acid by ultrasonic, then the hydrothermal reaction, the samples were washed to neutral, drying can be stably dispersed in the base oil of PAO6 graphite phase carbon nitride materials. The method has the advantages of simple preparation, no pollution and can be used for industrial production.
【技术实现步骤摘要】
一种亲油性改性石墨相氮化碳的制备方法
本专利技术涉及一种改性石墨相氮化碳的制备,具体涉及一种基于有机试剂改性获取得到亲油性提高的石墨相氮化碳的制备方法。
技术介绍
石墨相氮化碳具有类似于石墨的层状结构,层内的C、N原子相间排列,以σ键连接成六边形结构;其层间距为0.325nm,略小于石墨的层间距。由于其特殊的结构性质,通常作为一种半导体光催化剂。另外,石墨相氮化碳层与层之间由范德华力相连且层间可以滑移,是一种软质相,在润滑与摩擦方面具有较好的应用前景。但石墨相氮化碳作为一种无机材料,很难溶解于有机溶剂中,更难与其他有机或无机材料均匀地复合,这极大限制了石墨相氮化碳在各个领域的发展与应用。改善石墨相氮化碳在不同溶剂的分散性和材料的相容性,成为扩展石墨相氮化碳应用领域亟待解决的问题。为此,研究人员对石墨相氮化碳进行了相应的有机改性。例如,文献《Developingapolymericsemiconductorphotocatalystwithvisiblelightresponse.》(ChemicalCommunications,2010.46(39):p.7325 ...
【技术保护点】
一种亲油性改性石墨相氮化碳的制备方法,其特征在于制备过程包括如下步骤:将石墨相氮化碳与有机改性剂混合后,加入冰醋酸中超声,然后转移到水热釜中进行水热反应,最后将样品洗涤至中性,干燥得到改性石墨相氮化碳。
【技术特征摘要】
1.一种亲油性改性石墨相氮化碳的制备方法,其特征在于制备过程包括如下步骤:将石墨相氮化碳与有机改性剂混合后,加入冰醋酸中超声,然后转移到水热釜中进行水热反应,最后将样品洗涤至中性,干燥得到改性石墨相氮化碳。2.根据权利要求1所述的改性石墨相氮化碳的制备方法,其特征在于石墨相氮化碳与有机改性剂的质量之比为1:(10~50)。3.根据权利要求1所述的改性石墨相氮化碳的制备方法,其特征在于石墨相氮化碳与冰醋酸...
【专利技术属性】
技术研发人员:王继刚,顾永攀,勾学军,
申请(专利权)人:张家港市东大工业技术研究院,
类型:发明
国别省市:江苏,32