The invention relates to a preparation method of a high performance composite cobalt boride, including salt reaction, acid replacement reaction, boron acylation reaction with stearic acid and propionic acid instead of neodecanoate boronacylate controlled the degree of realization of the carbon number of alkyl cobalt boroacylate molecule consists of 3, 10 18, and the average control in 10, improve the dispersion of cobalt boroacylate products, improve the uniformity of rubber covering surface of steel cord, solve practical problems punctualstriation surface exposed adhesive, the adhesive rubber and steel cord rate reached more than 90%, promote the adhesion of rubber with a steel cord, prolong the service life of tire.
【技术实现步骤摘要】
本专利技术涉及硼酰化钴的制备方法。
技术介绍
硼酰化钴，其理论分子式为：（RmCO－Co－O－）3B，（式中m=3～11，以9为主）。硼酰化钴是一种活性较高的粘合促进剂，主要用于天然橡胶、合成橡胶或这些胶与黄铜、锌、裸铜及镀黄铜或锌的钢丝帘线、绳、金属板的粘合促进。它是以氢氧化钴和醋酸及相关有机酸为原料，先进行酸碱成盐反应，而后再进行硼酰化反应。由该方法制备的硼酰化钴含钴量较高，它们在橡胶硫化时，反应活性大，对橡胶与钢丝的粘合增强起主要作用，但缺点是其在橡胶制品中分散性差而引起附胶（附胶率：橡胶渗透到钢帘线中覆盖钢帘线表面的程度）不均匀，直接影响橡胶与钢帘线的粘合强度和耐老化性能的不稳定。公布号CN103113416A的专利公开了一种低熔点硼酰化钴的制备方法，其中和反应是将新癸酸、丙酸、戊酸、硬脂酸、松香、二甲苯与氢氧化钴混合进行酸碱中和反应，中和反应完成后得到中间产物。由于中和反应中原料中酸的种类较多，且中和反应一锅式进行，中和反应产物中取代混乱，在后面的硼酰化反应后，产物中的烃基的取代无规律，单一硼酰化钴中烃基的碳数目分布较广，整个硼酰化程度难以控制，导致硼...
【技术保护点】
一种高性能复合型硼酰化钴的制备方法，其特征在于：包括如下步骤，步骤一、成盐反应以氢氧化钴和丙酸为原料，在常压密封容器中，温度100～150℃，时间≥2小时，反应生成丙酸钴，其反应式为： CO(OH)2 + CH3CH2COOH à CH3CH2－CO－O－Co－O－CO－CH3CH2 +2 H2O；步骤二、酸置换反应在上述反应体系中加入新癸酸和硬脂酸，控制温度150～190℃，时间≥2小时，反应置换出丙酸钴分子中的一个丙酸；其反应式为：+ CH3(CH2)8COOH àRn+CH3CH2COOH+ CH3(CH2)16COOH àRm+CH3CH2COOH其中：n=9， m...
【技术特征摘要】
1.一种高性能复合型硼酰化钴的制备方法，其特征在于：包括如下步骤，步骤一、成盐反应以氢氧化钴和丙酸为原料，在常压密封容器中，温度100～150℃，时间≥2小时，反应生成丙酸钴，其反应式为：CO(OH)2+CH3CH2COOHàCH3CH2－CO－O－Co－O－CO－CH3CH2+2H2O；步骤二、酸置换反应在上述反应体系中加入新癸酸和硬脂酸，控制温度150～190℃，时间≥2小时，反应置换出丙酸钴分子中的一个丙酸；其反应式为：+CH3(CH2)8COOHàRn+CH3CH2COOH+CH3(CH2)16COOHàRm+CH3CH2COOH其中：n=9，m=17经过上述步骤一和二后得到下面三种钴盐的混合盐:...
【专利技术属性】
技术研发人员：徐京海，陶秀军，李雷，
申请(专利权)人：江阴市三良橡塑新材料有限公司，
类型：发明
国别省市：江苏;32