The present invention provides an excellent alignment film of syndiotactic polystyrene resin in the suppression of heat damage caused by wrinkle during high temperature heat treatment. That is, to provide an orientation film, the orientation film is made of resin composition, the resin composition comprising a syndiotactic structure of styrenic polymer resin as main component, and comprises a glass transition temperature of 130 DEG C or more amorphous thermoplastic resin; heat shrinking by 130 DEG C 30 minutes heat treatment when the plane direction rate is below 5%, thermal shrinkage under 200 DEG C for 10 minutes after heat treatment when the in-plane direction of at least one direction rate is above 6.5%.
【技术实现步骤摘要】
【国外来华专利技术】取向膜
本专利技术涉及由间规(syndiotactic)结构的苯乙烯系聚合物构成的取向膜。进一步详细而言，涉及因进行蒸镀工序等高温下的热处理时的折皱而引起的热损害发生得到抑制的由间规结构的苯乙烯系聚合物构成的取向膜。
技术介绍
以往，膜电容器通过如下方法制造：将双轴取向聚对苯二甲酸乙二醇酯膜、双轴取向聚丙烯膜等膜与铝箔等金属薄膜重叠，并进行缠绕或叠层的方法。近年来，随着电气或电子线路小型化的要求，膜电容器的小型化、可安装化也正在发展，除了电气特性以外并且还要求耐热性。另外，在汽车用途中，不仅在驾驶室内使用，使用范围还扩大到发动机室内，除了电气特性以外，还要求适合更为高温高湿下的环境的膜电容器。针对上述要求，专利文献1(日本特开平2-143851号公报)、专利文献2(日本特开平3-124750号公报)、专利文献3(日本特开平5-200858号公报)、专利文献4(国际公开2008/156210号小册子)中提出了使用耐热性和电气特性优异的极薄的间规聚苯乙烯系膜的方法。并且，日本特开2011-111592号公报中，为了使间规聚苯乙烯系膜的耐热性提高、且使制膜性提高，提出了...
【技术保护点】
取向膜，其特征在于，所述取向膜由树脂组合物构成，所述树脂组合物包含间规结构的苯乙烯系聚合物作为主要的树脂成分，且包含玻璃化转变温度为130℃以上的热塑性非晶树脂；130℃下经30分钟热处理时的面内方向的热收缩率为5.0％以下，200℃下经10分钟热处理时的面内方向的至少一个方向的热收缩率为6.5％以上。
【技术特征摘要】
【国外来华专利技术】2014.11.18 JP 2014-2335601.取向膜，其特征在于，所述取向膜由树脂组合物构成，所述树脂组合物包含间规结构的苯乙烯系聚合物作为主要的树脂成分，且包含玻璃化转变温度为130℃以上的热塑性非晶树脂；130℃下经30分钟热处理时的面内方向的热收缩率为5.0％以下，200℃下经10分钟热处理时的面内方向的至少一个方向的热收缩率为6.5％以上。2.权利要求1所述的取向膜，其中，振动频率10Hz下的损耗弹性模量...
【专利技术属性】
技术研发人员：中西贵之，羽田正纪，吉田哲男，
申请(专利权)人：帝人株式会社，
类型：发明
国别省市：日本,JP