The invention provides an improved electrode aluminum foil treatment method for a solid capacitor, which includes pretreatment, primary corrosion, medium treatment, two corrosion, post-treatment, drying and the like. The postprocessing method is two times of corrosion treated by aluminum foil washing, 1 ~ 10wt% and 0.2 ~ 2wt% sulfuric acid aluminum sulfate mixed solution with 50 350 seconds, followed by 1 ~ 25wt% triethanolamine aqueous solution, after washing 150 500 drying. 20 30% lower leakage current compared with the original process after formation leakage current obtained by the process of corrosion of the foil, suitable for the production of solid electrolytic capacitor.
【技术实现步骤摘要】
一种后处理改进型的固态电容器用电极铝箔处理方法
本专利技术主要涉及固态电容器电极铝箔的制造工艺方法，具体涉及降低电极铝箔的漏电电流技术。
技术介绍
20世纪90年代以来，固态铝电解电容器凭借着高稳定性、寿命长、低ESR和高额定纹波电流成为我国主要的电容产业。随着我国电子的快速发展，对电容器的需求也越来越高，这也意味着对固态电容器静电容量的要求也越来越高。在以往的提高方法中会出现其他方面的降低，比如机械强度。以前，固态电容器用电极箔生产，一般都是将99.99％铝箔经前处理，一次腐蚀，中间处理，二次腐蚀，再用硝酸或磷酸浸泡后水洗干净烘干，但后继续化成后漏电流较大，这使做成固态铝电解电容器容易过早干凅失效。
技术实现思路
专利技术目的：针对上述存在的问题和缺陷，本专利技术提出一种后处理改进型的固态电容器用电极铝箔处理方法，得到的电极箔形成后漏电流小，适用于生产固态铝电解电容器。技术方案：为达到上述专利技术目的，本专利技术采用以下技术方案：一种后处理改进型的固态电容器用电极铝箔处理方法，包括以下步骤：(1)前处理：铝箔浸在含有0.1～10wt％磷酸的水溶液中，并在25～85℃...
【技术保护点】
一种后处理改进型的固态电容器用电极铝箔处理方法，其特征在于包括以下步骤：(1)前处理：铝箔浸在含有0.1～10wt％磷酸的水溶液中，并在25～85℃温度下浸泡50～350s；(2)一次交流腐蚀：将前处理后的铝箔放在含有2～20wt％盐酸和0.2～20wt‰三氯化铝的混合溶液中进行交流腐蚀，腐蚀温度为18～55℃、电流密度为5～50A/dm
【技术特征摘要】
1.一种后处理改进型的固态电容器用电极铝箔处理方法，其特征在于包括以下步骤：(1)前处理：铝箔浸在含有0.1～10wt％磷酸的水溶液中，并在25～85℃温度下浸泡50～350s；(2)一次交流腐蚀：将前处理后的铝箔放在含有2～20wt％盐酸和0.2～20wt‰三氯化铝的混合溶液中进行交流腐蚀，腐蚀温度为18～55℃、电流密度为5～50A/dm2，腐蚀10～80秒；(3)中间处理：将经过一次交流腐蚀后的铝箔放在温度为25～90℃，含有0.5～10wt％磷酸和5～30wt％盐酸的水溶液中浸泡50～350秒；(4)二次腐蚀：将经过中处理后铝箔作为阳极进行多级扩孔腐蚀，放在温度为10～50℃，含有...