The invention discloses a high toughness and high wear resistance of polystyrene and its preparation method, basic formula and weight ratio were: high impact polystyrene 35 45, thermoplastic polyurethane 15 25 copies, 20 copies, 12 toughening agent polyfunctional chain extender 5 14, maleic anhydride graft copolymer 6 12 copies, 10 copies of 4 rare earth coupling agent, inorganic antifriction agent 10 20 copies, 5 copies of antioxidant 1. The preparation method of the invention is to send the material evenly mixed into the feeding hopper of the double screw extruder and extrude and granulate through the double screw extruder. The polystyrene plastic prepared by the invention has high mechanical strength, good abrasion resistance and toughness, and is suitable for packaging materials, automobile interior decoration and other fields.
【技术实现步骤摘要】
一种高韧性高耐磨聚苯乙烯塑料及其制备方法
本专利技术涉及高分子材料领域，尤其涉及一种高韧性高耐磨聚苯乙烯塑料及其制备方法。
技术介绍
聚苯乙烯为无毒、无臭、无色的透明颗粒，是当今广泛应用的大品种合成树脂之一。这种传统的聚苯乙烯的制品具有极高的透明度，透光率可达90％以上，电绝缘性能好，易着色，加工流动性好，刚性好及耐化学腐蚀性好，价格低廉等优点。但是，普通的聚苯乙烯材料存在许多不足之处，不耐磨、力学强度低等，这些缺点都大大限制了聚苯乙烯的应用范围。为改变聚苯乙烯材料不耐磨、力学强度低的缺点，一般通过添加玻璃纤维进行改性以达到工程塑料级别的应用。但由于聚苯乙烯是一种非极性材料，所以与极性玻璃纤维界面粘结差。但是一般这样的改性材料添加有大量玻璃纤维，会给材料带来负面的影响，如脆性、冲击强度低、易出现开裂等，一定程度上限制了聚苯乙烯的应用。
技术实现思路
本专利技术目的在于克服现有技术中的缺陷，提供一种高韧性高耐磨聚苯乙烯塑料,其力学强度高、耐磨损和韧性好。同时，本专利技术还提供了一种高韧性高耐磨聚苯乙烯塑料的制备方法。为达到上述目的，本专利技术是通过以下技术方案实现的：一...
【技术保护点】
一种高韧性高耐磨聚苯乙烯塑料，其特征在于，基本配方和重量比组成为：高抗冲聚苯乙烯 35‑45份、热塑性聚氨酯 15‑25份、增韧剂12‑20份、多官能团扩链剂5‑14份、马来酸酐接枝共聚物 6‑12份、稀土偶联剂 4‑10份、无机耐磨剂10‑20份、抗氧剂1‑5份。
【技术特征摘要】
1.一种高韧性高耐磨聚苯乙烯塑料，其特征在于，基本配方和重量比组成为：高抗冲聚苯乙烯35-45份、热塑性聚氨酯15-25份、增韧剂12-20份、多官能团扩链剂5-14份、马来酸酐接枝共聚物6-12份、稀土偶联剂4-10份、无机耐磨剂10-20份、抗氧剂1-5份。2.根据权利要求1所述的高韧性高耐磨聚苯乙烯塑料，其特征在于：所述热塑性聚氨酯为聚醚型热塑性聚氨酯。3.根据权利要求1所述的高韧性高耐磨聚苯乙烯塑料，其特征在于：所述增韧剂为废旧橡胶轮胎粉末，目数为2000目-3000目。4.根据权利要求1所述的高韧性高耐磨聚苯乙烯塑料，其特征在于：所述多官能团扩链剂为三羟甲基丙烷、丙三醇中的至少一种。5.根据权利要求1所述的高韧性高耐磨聚苯乙烯塑料，其特征在于：所述马来酸酐接枝共聚物为马来酸酐接枝E...
【专利技术属性】
技术研发人员：刘凤姐，
申请(专利权)人：泉州盈创新材料技术开发有限公司，
类型：发明
国别省市：福建,35