The invention discloses a silver framework for the specification of the production method, which comprises the following steps: drawing the frame pattern then line on paper cutting out the frame shape, the frame form a block without disconnecting the whole; placed in a frame of flat metal plate leveling, and then take the silver wire fill in within the framework of the framework; will fill the silver fire, firing 3 repeated 4 times, 200 firing temperature of 300 DEG C, the soft silver after leveling, add borax, and put it on the flat metal plate, welding powder for welding reinforcement, forming; forming products on the alum solution in use gas heating and boiling, to be white accessories, products will be removed, and then water again after boiling water. The design of the silver frame has strong stereoscopic feeling, clear lines and vivid patterns.
【技术实现步骤摘要】
一种纯银框架的规范制作方法
本专利技术涉及纯银工艺品的制作方法，尤其是一种纯银框架的规范制作方法。技术背景银饰作为一种文化现象在历史上被许多民族青睐，成为多元文化交流的载体之一，苗族银饰全系手工制作，有30多道工序，形成熔铸、锤打、焊接，编结、洗涤等一整套工艺；纯银编丝工艺的银饰制作是将各种拉好的银丝组件合成的过程，编结时辅以纯银拉丝焊接方法等工艺的使用，将不同的组件固定在一起焊接成型。然而纯银工艺品的制作方法中存在差异，产品质量不稳定，部分纯银工艺品立体感差，纹路不清晰，不能体现工艺品的精美价值。
技术实现思路
针对现有技术的不足之处，本专利技术旨在提供一种纯银框架的规范制作方法，使银饰的图案立体感强、纹路清晰、质量稳定。为达成上述目的，本专利技术采用的技术方案：一种纯银框架的规范制作方法，包括如下操作步骤：1）在纸张上绘制框架图案，根据绘制的框架图案，再用线切割加工出框架形状，使框架形成一块无断接整体；2）将整幅框架置放在一块较为平整的金属板上整平，然后取足量压扁的银丝在框架内填丝；3）将填满银丝的框架，用火反复烧制3-4次，烧制温度200-300℃，使银丝柔...
【技术保护点】
一种纯银框架的规范制作方法，其特征在于包括如下操作步骤：1）在纸张上绘制框架图案，根据绘制的框架图案，再用线切割加工出框架形状，使框架形成一块无断接整体；2）将整幅框架置放在一块较为平整的金属板上整平，然后取足量压扁的银丝在框架内填丝；3）将填满银丝的框架，用火反复烧制3‑4次，烧制温度200‑300℃，使银丝柔软后整平，放入硼砂水，取出放置在平整的金属板上，用焊粉进行烧焊，加固成形，所述硼砂水为硼砂0.5克，水250克配制；4）将成形的产品放在明矾溶液中，用猛火加温煮沸，待饰品雪白时，将产品取出后，再用清水又一次煮沸后清水即可，明矾溶液为明矾1克，水10克配制。
【技术特征摘要】
1.一种纯银框架的规范制作方法，其特征在于包括如下操作步骤：1）在纸张上绘制框架图案，根据绘制的框架图案，再用线切割加工出框架形状，使框架形成一块无断接整体；2）将整幅框架置放在一块较为平整的金属板上整平，然后取足量压扁的银丝在框架内填丝；3）将填满银丝的框架，用火反复烧制3-4次，烧...
【专利技术属性】
技术研发人员：杨平生，
申请(专利权)人：凯里市杨平生银饰有限公司，
类型：发明
国别省市：贵州,52