一种高介高频电子陶瓷介质材料及制备方法技术

本发明专利技术公开了一种高介高频电子陶瓷介质材料及制备方法，该组别电子陶瓷介质材料具有特定的介电常数，适合于制作大容量高频陶瓷电容器、大功率陶瓷电容器、超高压陶瓷电容器等，主要由二氧化钛、钛酸锶、氧化锆、氧化锌、碳酸锂、粘土、氧化钐、五氧化二钒按照一定比例，采用科学的生产工艺制成。通过检测和用户使用证明，其介质常数、介质损耗、抗电强度、绝缘电阻等性能指标均明显优于现有技术。

High dielectric high frequency electronic ceramic dielectric material and preparation method thereof

The invention discloses a high frequency electronic dielectric ceramic dielectric material and preparation method has specific dielectric constant of the group of electronic ceramic materials, suitable for the production of large capacity high frequency high power ceramic capacitor, ceramic capacitor, super high voltage ceramic capacitor, mainly composed of titanium dioxide, zirconium oxide, strontium titanate, Zinc Oxide, lithium carbonate, clay, samarium oxide, five of two vanadium according to a certain proportion, made the scientific process. The performance of dielectric constant, dielectric loss, dielectric strength and insulation resistance are obviously superior to those of existing technology through detection and user's use.

【技术实现步骤摘要】
一种高介高频电子陶瓷介质材料及制备方法
本专利技术属于电子新材料
，尤其涉及一种高介高频电子陶瓷介质材料及制备方法。
技术介绍
电子陶瓷介质材料主要用来制作陶瓷电容器，其中的UJ组别高频瓷料主要用于制作大容量高频陶瓷电容器、大功率陶瓷电容器、超高压陶瓷电容器等，主要用于制备高电容电容器、多层基片、各种传感器等。随着电子科学的不断发展，对介电陶瓷性能要求是越来越高，钛酸锶陶瓷是一种新的多功能电子陶瓷材料，它具有介电损耗低、温度稳定性好等优点。有研究表明:钛酸锶的四角相态点的相转移温度为108K，纯SrTiO3的居里温度是35K甚至更低。SrTiO3不仅具有高的电容率和低的耗散因子，而且具有良好的温度稳定性和抗高电压性。可用于制造高电压和高电容率的陶瓷电容器。钛酸锶粉体的制备方法也是研究的热点，现已开发出许多化学液相粉体制备方法，如溶胶-凝胶法、共沉淀法、水热合成法等。国内已有厂家生产该瓷料，但有介电常数小、耐压不高、损耗大、性能不稳定等缺点，不能用于制作大容量的高频高压电容及要求较严的场合。
技术实现思路
本专利技术的目的是提供一种高介高频电子陶瓷介质材料及制备方法。本专利技术的目的本文档来自技高网...

【技术保护点】
一种高介高频电子陶瓷介质材料，其特征在于该高介高频电子陶瓷介质材料由以下材料制成：二氧化钛（TiO

【技术特征摘要】
1.一种高介高频电子陶瓷介质材料，其特征在于该高介高频电子陶瓷介质材料由以下材料制成：二氧化钛（TiO2）80～90%，钛酸锶(SrTiO3)4～10%，氧化锆(ZrO2)2～8%，氧化锌(ZnO)0.2～1%，碳酸锂(Li2CO3)0.2～1%，粘土0.2～1%，氧化钐(Sm2O3)0.1～0.6%，五氧化二钒(V2O5)0.1～0.6%。2.如权利要求1所述的一种高介高频电子陶瓷介质材料，其特征在于该高介高频电子陶瓷介质材料由以下材料制成：二氧化钛（TiO2）85%，钛酸锶(SrTiO3)7%，氧化锆(ZrO2)5%，氧化锌(ZnO)0.6%，碳酸锂(Li2...

【专利技术属性】
技术研发人员：赵华，
申请(专利权)人：临沂金成电子有限公司，
类型：发明
国别省市：山东,37