The present invention relates to a welding tractor, idler for submerged arc welding of flux cored wire and method of use thereof, comprises the following components: the mass fraction of aluminum magnesium alloy powder is 1 ~ 1.5%, 3 ~ 3.7% electrolytic manganese powder, silicon carbide is 2 ~ 2.6%, 3 ~ 4% of vanadium iron, Mo ranged from 0.5 to 0.9%, the balance water spray powder method. The invention uses welding, welding process behavior with good flux cored wire submerged arc welding, surfacing layer has the plasticity and toughness and impact resistance, can realize multi-layer welding, good wear resistance, thus formed on the workpiece surface abrasion resistance, good corrosion resistance of the welding layer, prolong the service life of workpieces.
【技术实现步骤摘要】
拖拉机惰轮的堆焊、埋弧焊用管状焊丝及其使用方法
本专利技术涉及焊接加工
，具体地说是拖拉机惰轮的堆焊、埋弧焊用管状焊丝及其使用方法。
技术介绍
拖拉机惰轮在日常的使用过程中，会出现一定程度的磨损，当磨损量超出一定值后，会导致动力传递收到一定程度影响。若更换新的拖拉机惰轮，则成本较高，磨损后的拖拉机惰轮会被丢弃而导致严重的资源浪费。目前有通过焊接增材的方式实现对磨损后的拖拉机惰轮的修复，从而使得拖拉机惰轮可以重复再利用，有效的避免了资源的浪费，但是这种修复并不能对拖拉机惰轮的性能如耐磨性和耐腐蚀性进行改善，导致使用寿命较短，反复的修复成本较高。
技术实现思路
为了解决现有技术中的不足，本专利技术提出拖拉机惰轮的堆焊、埋弧焊用管状焊丝及其使用方法。本专利技术所要解决的技术问题采用以下技术方案来实现：拖拉机惰轮的堆焊、埋弧焊用管状焊丝，包括以下质量百分比的组分：铝镁合金粉为1～1.5％，电解锰粉为3～3.7％，碳化硅为2～2.6％，钒铁粉为3～4％，Mo为0.5～0.9％，余量为水雾法铁粉。拖拉机惰轮的堆焊、埋弧焊用管状焊丝的使用方法，所述方法步骤如下：第一步：工件的...
【技术保护点】
拖拉机惰轮的堆焊、埋弧焊用管状焊丝，其特征在于：包括以下质量百分比的组分：铝镁合金粉为1～1.5％，电解锰粉为3～3.7％，碳化硅为2～2.6％，钒铁粉为3～4％，Mo为0.5～0.9％，余量为水雾法铁粉。
【技术特征摘要】
1.拖拉机惰轮的堆焊、埋弧焊用管状焊丝，其特征在于：包括以下质量百分比的组分：铝镁合金粉为1～1.5％，电解锰粉为3～3.7％，碳化硅为2～2.6％，钒铁粉为3～4％，Mo为0.5～0.9％，余量为水雾法铁粉。2.拖拉机惰轮的堆焊、埋弧焊用管状焊丝的使用方法，其特征在于：所述方法步骤如下：第一步：工件的预处理：去除工件表面上的油污、锈；第二步：确定焊丝直径和焊接电流、电压；第三步：通过焊机将焊丝焊接在工件表面，焊速控制在450～570mm/min。3.根据权利要...
【专利技术属性】
技术研发人员：程敬卿，周乾坤，
申请(专利权)人：安徽再制造工程设计中心有限公司，
类型：发明
国别省市：安徽,34