本发明专利技术目的是提供一种合成工艺绿色环保，操作简单明了的喷丝板脱模剂的合成方法，并且合成的喷丝板脱模剂具有粘度大、耐热性和耐氧化性强、热失重小、成膜时间短、保板时间长等优点。本方法以二甲基硅油、苯基硅油、含氢硅油为原料，加入硝酸盐催化剂，然后经过保温回流，升温蒸馏，减压蒸馏三个过程最终制得改性硅油，最后将改性硅油与溶剂以及抛射剂一起压罐便可得到喷丝板脱模剂。

Synthetic technology of spinneret releasing agent

The aim of the invention is to provide a synthesis of green environmental protection, spinneret release agent synthesis method is simple and straightforward, and spinneret release agent synthesis has the advantages of high viscosity, heat resistance and oxidation resistance, thermal stability, strong film short time and long time holding plate. This method to two methyl phenyl silicone oil, silicone oil, silicone oil containing hydrogen as raw material, adding nitrate catalyst, and then after heat reflux, heating distillation, vacuum distillation process to produce three modified silicone oil, the modified silicone oil and solvent and the propellant tank can be pressed to a spinneret release agent.

【技术实现步骤摘要】
喷丝板脱模剂的合成技术
本专利技术涉及喷丝板脱模剂的合成技术。主要适用于熔融纺丝过程中喷丝板的清洗及润滑，以提高纺丝的质量。
技术介绍
喷丝板脱模剂是合成纤维纺丝过程中经常用到的一种润滑剂。其具有低温下快速成膜，成膜时间短，耐高温性能好的特点。化学纤维在纺丝过程中由于长时间使用纺丝的粘板作用会在喷丝板上形成污垢导致纺丝断丝的现象，因此需要对喷丝板进行清洗并在喷丝板上形成一层持久的保护膜，以保证纺丝顺利进行。因此这层保护膜是保证化学纤维顺利纺丝的关键。而雾化硅油就是作为这层保护膜使用的助剂。但在雾化硅油合成的传统工艺中使用的反应溶剂为苯，其毒性较大，对环境有害。因此寻找绿色环保型溶剂以代替传统工艺中的苯作为反应溶剂并探寻出以新型溶剂为反应溶剂合成雾化硅油的最佳工艺条件是亟待解决的一大问题。另外，引入新的有机基团以提高雾化硅油的保板时间也是迫切需要解决的又一问题。本专利技术涉及的喷丝板脱模剂的合成方法比较简单，使用大的反应溶剂绿色环保，而且合成工艺简单易行，生产成本较低，适合大规模生产，使这类喷丝板脱模剂的工业化成为可能。
技术实现思路
本专利技术目的是提供一种合成工艺绿色环保，操作简单明了本文档来自技高网...

【技术保护点】
喷丝板脱模剂的合成方法，其原理如下：第一步

【技术特征摘要】
1.喷丝板脱模剂的合成方法，其原理如下：第一步第二步第一步中制备的改性硅油与溶剂和抛射剂混合压罐得到最终产物喷丝板脱模剂。2.权利要求1中所述，二甲基硅油粘度(25℃)345.49mm2/s；含氢硅油，活性氢质量分数为1.6％，黏度20mm2/s。3.权利要求1中所述，催化剂为硝酸铈铵。4.权利要求1中所述，二甲基硅油、苯基硅油、含氢硅油体积比为90∶20∶1。5.权利要求1中所述，反应投料顺序分别环己烷...