一种PE水性热熔胶及其制备方法技术

本发明专利技术公开了一种PE水性热熔胶，配方按重量百分比为：丙烯酸或甲基丙烯酸1～8％、甲基丙烯酸甲酯5～20％、丙烯酸酯10～40％、乳化剂0.5～5％、自由基引发剂0.1～0.5％、去离子水40～80％，同时还公开了其制备方法。由于采用去离子水为溶剂，可以降低成本和减少有机溶剂的使用，而生成后的PE水性热熔胶为液态，流动性强，可刷、浸、淋、喷等，使用方便，同时粘着力强，初粘力大于12(球号)，而持粘力大于24小时，180度剥离强度大于6.86N/25mm。

PE water based hot melt adhesive and preparation method thereof

The invention discloses a PE water hot melt adhesive formula by weight percent: acrylic acid or methacrylic acid methyl methacrylate, 1 ~ 8% 5 ~ 20%, 10 ~ 40%, acrylate emulsifier is 0.5 ~ 5%, 0.1 ~ 0.5% free radical initiator, deionized water 40 ~ 80% at the same time, the system also discloses the preparation methods. By using deionized water as solvent, can reduce the cost and reduce the use of organic solvents, and PE water after the hot melt into liquid, strong liquidity, can brush, dip, spray, spray, easy to use, and strong adhesion, adhesion is greater than 12 (ball), and stick the force is more than 24 hours, 180 degree peel strength is greater than 6.86N/25mm.

【技术实现步骤摘要】
一种PE水性热熔胶及其制备方法
本专利技术涉及胶粘剂领域，具体涉及一种PE水性热熔胶及其制备方法。
技术介绍
胶水是连接两种材料的中间体，多以水剂出现，属精细化工类，种类繁多，主要以粘料、物理形态、硬化方法和被粘物材质的分类方法。常见的有瞬间胶、环氧树脂粘结类、厌氧水溶性热熔胶、UV水溶性热熔胶、热熔胶、压敏胶、乳胶类等，该类传统的固态热熔胶在使用时需要经过多道工序，不利于使用，同时使用时其粘连结果不佳，影响后期需粘连产品的质量。因此，亟需一种使用方便，并且粘着力强的PE水性热熔胶。
技术实现思路
本专利技术要解决的技术问题是提供一种PE水性热熔胶，该热熔胶使用方便，常温下为液状，同时粘着力强，能满足粘结需求。为了解决上述技术问题，本专利技术的技术方案为一种PE水性热熔胶，其配方按重量百分比如下：优选地，乳化剂为脂肪醇聚氧乙烯醚、失水山梨醇脂肪酸酯、烷基酚聚氧乙烯醚按重量比l：1：2混合而成。一种PE水性热熔胶，其制备方法为：先将乳化剂溶于去离子水，再将丙烯酸或甲基丙烯酸、甲基丙烯酸甲酯、丙烯酸酯加入乳化剂溶液进行预乳化，形成乳化液；将1/4～1/3的乳化液倒入反应釜中搅拌，同时加热至6本文档来自技高网...

【技术保护点】
一种PE水性热熔胶，其特征在于，配方按重量百分比如下：

【技术特征摘要】
1.一种PE水性热熔胶，其特征在于，配方按重量百分比如下：2.根据权利要求1所述的PE水性热熔胶，其特征在于，所述乳化剂为脂肪醇聚氧乙烯醚、失水山梨醇脂肪酸酯、烷基酚聚氧乙烯醚按重量比l：1：2混合而成。3.一种权利要求1或2所述的PE水性热熔胶的制备方法，其特征在于，制备步骤为：先将乳化剂溶于去离子水，再将丙烯酸或甲基丙烯...