The invention relates to a production method of high fluidity of titanium dioxide, specifically, the invention relates to a coating process with high fluidity of titanium dioxide used in the laminated paper, which comprises the following steps: coating trough into titanium dioxide slurry, slurry concentration and detection of PH 20min in the slurry; heating up to 40 DEG C; 60min in the slurry is heated to 80 DEG C; adding dilute phosphoric acid in 30min adjusted PH 10; and 60min in dilute phosphoric acid sodium metaaluminate and flow; dilute sulphuric acid and sodium aluminate in 150min and flow, and flow of PH was 7 7.5; with dilute sulfuric acid to adjust the pH value of slurry, coated. Beam. The product obtained by the coating method has good performance, in particular, the brightness of the product is improved, the cost is reduced, and the pollution to the environment is reduced.
【技术实现步骤摘要】
一种高流动性钛白粉的生产方法
本专利技术涉及一种钛白粉的包膜方法，具体地讲，本专利技术涉及在层压纸中使用的高流动性钛白粉的包膜工艺。
技术介绍
钛白粉是一种白色颜料，广泛应用于涂料、化纤、橡胶、搪瓷、陶瓷、塑料、造纸、印刷油墨、电子陶瓷、玻璃、焊条、化妆品等工业。金红石钛白粉若需获得较好的耐候性、分散性等优良的应用性能，必须经过无机表面处理，在其表面均匀地包覆一层无机氧化物膜。然而，根据目前的相关文献和专利报道，尚未出现关于在层压纸中使用的高流动性钛白粉的包膜工艺。
技术实现思路
本专利技术针对现有技术中存在的不足，本专利技术的目的之一在于解决上述现有技术中存在的一个或多个问题。本专利技术的目的之一在于提供一种在层压纸中使用的高流动性钛白粉的包膜工艺。为了实现上述目的，本专利技术采用的技术方案为：一种高流动性钛白粉的生产方法，其特征在于，钛白粉的包膜工艺包括以下步骤：在包膜槽进钛白粉料浆并检测料浆PH和浓度；在20min内将料浆升温至40℃；在60min内将料浆升温至80℃；在30min加入稀磷酸调整PH为10.0；在60min内稀磷酸与偏铝酸钠并流；在150min内...
【技术保护点】
一种高流动性钛白粉的生产方法，其特征在于：钛白粉的包膜工艺包括以下步骤：在包膜槽进钛白粉料浆并检测料浆的PH和浓度；在20min内将料浆升温至40℃；在60min内将料浆升温至80℃；在30min加入稀磷酸调整PH为10.0；在60min内稀磷酸与偏铝酸钠并流；在150min内稀硫酸与偏铝酸钠并流，并流PH为7.0‑7.5；用稀硫酸调整料浆PH值，包膜结束。
【技术特征摘要】
1.一种高流动性钛白粉的生产方法，其特征在于：钛白粉的包膜工艺包括以下步骤：在包膜槽进钛白粉料浆并检测料浆的PH和浓度；在20min内将料浆升温至40℃；在60min内将料浆升温至80℃；在30min加入稀磷酸调整PH为10.0；在60min内稀磷酸与偏铝酸钠并流；在150min内稀硫酸与偏铝酸钠并流，并流PH为7.0-7.5；用稀硫酸调整料浆PH值，包膜结束。2.根据权利要求1所述的一种高流动性钛白粉的生产方法，其特征在于，所述钛白粉浆料的浓度为2...
【专利技术属性】
技术研发人员：卢慧军，胡海军，唐臣成，
申请(专利权)人：襄阳龙蟒钛业有限公司，
类型：发明
国别省市：湖北,42