The invention discloses a high retention of the reconstituted tobacco paper base preparation method, the konjac gum with hydrogen peroxide oxidation, and plant protein, aluminum sulfate mixture on calcium carbonate was modified, and then mixing the slurry after tobacco sheet, vacuum drying, drying processes, are made of tobacco paper base. The production process of the invention is simple and easy to operate, can effectively reduce the cost and save the raw materials, reconstituted tobacco paper base produced with excellent physical properties and appearance quality, and does not affect the smoking quality of reconstituted tobacco, strong practicability.
【技术实现步骤摘要】
一种高留着的再造烟叶纸基制备方法
本专利技术涉及烟叶生产
，尤其涉及一种高留着的再造烟叶纸基制备方法。
技术介绍
造纸法再造烟叶(又称“薄片”)是指按再造烟叶原料配方要求，将烟末、烟梗等原料用溶剂浸泡提取后，分离出可溶性物质和不溶性物质，将不溶性物质用造纸的方法制成像原纸一样的烟片基，然后存该片基上加入浓缩后的可溶性物质和添加剂，干燥后成为再造烟叶。与辊压法和稠浆法薄片相比，造纸法再造烟叶具有填充性能好、焦油释放量低等优点，具有广阔的发展前景。目前再造烟叶纸基生产常用的填料为沉淀碳酸钙，其在再造烟叶纸基中的留着率低，不仅造成浆料的利用率低，还会影响再造烟叶的产量和质量。因此，提高浆料留着率已经成为备受关注的研究课题。CN103859576A通过天然马铃薯淀粉对填料进行表面包裹或部分包裹、调节表面电荷、然后将包裹的填料加入烟草浆料中生产造纸法再造烟叶，有效提高了浆料中纤维和填料的留着，提高了原料的利用率，并对烟草薄片品质无影响。然而这种方法仅改善了浆料留着率，对再造烟叶纸基的物理性能指标并没有提升，同时马铃薯淀粉作为包裹剂，对填料以及纤维的附着性较低，对浆料留...
【技术保护点】
一种高留着的再造烟叶纸基制备方法，其特征在于，包括以下步骤：（1）先将3‑5重量份魔芋胶加入60‑80重量份水中于60‑80℃充分搅拌1‑2h，然后用氢氧化钠将pH调至9‑9.5，加入1‑1.5重量份双氧水继续搅拌0.5‑1h，冷却后得改性魔芋胶溶液；（2）将20‑30重量份碳酸钙与10‑15重量份步骤（1）的改性魔芋胶溶液充分混合，再加入0.1‑0.15重量份植物蛋白继续搅拌，然后加入0.1‑0.15重量份硫酸铝高速混合并研磨均匀，得改性碳酸钙；（3）将80‑100重量份烟梗、烟末打浆制得的烟草浆料与40‑80重量份步骤（2）的改性碳酸钙混合均匀，经过抄片、真空干燥、烘干...
【技术特征摘要】
1.一种高留着的再造烟叶纸基制备方法，其特征在于，包括以下步骤：（1）先将3-5重量份魔芋胶加入60-80重量份水中于60-80℃充分搅拌1-2h，然后用氢氧化钠将pH调至9-9.5，加入1-1.5重量份双氧水继续搅拌0.5-1h，冷却后得改性魔芋胶溶液；（2）将20-30重量份碳酸钙与10-15重量份步骤（1）的改性魔芋胶溶液充分混合，再加入0.1-0.15重量份植物蛋白继续搅拌，然后加入0.1-0.15重量份硫酸铝高速混合并研磨均匀，得改性碳酸钙；（3）将80-100重量份烟梗、烟末打浆制得的烟草浆料与40-80重量份步骤（2）的改性碳酸钙混合均匀，经过抄片、真空干燥、烘干工序，即得...
【专利技术属性】
技术研发人员：陈长兵，阮学良，王铜根，
申请(专利权)人：天长市天达纸箱纸品厂，
类型：发明
国别省市：安徽,34