The invention discloses a polypropylene containing ammonium drilling additives and manufacturing method thereof, which is characterized in that contains the following parts by weight: 100 200 acrylic and water 600 800, polyacrylate 7 12 copies, 0.8 copies of the 1.2 polyacrylamide, cross-linking 5, 10 agent 50 60 nanmu powder samples. The present invention further reduce mud filtration and apparent viscosity, avoid the npan must be large (2.1Mpa around) below the pressure conditions can not brings security risks of production, reduce the use amount of mud additives, improve product potency ratio, thereby reducing the drilling cost effectively.
【技术实现步骤摘要】
一种含聚丙烯铵盐的石油钻井助剂及其制造方法
本专利技术涉及一种含聚丙烯铵盐的石油钻井助剂及其制造方法。
技术介绍
在石油钻井作业中,业内人士常常用澎润土加水制成钻井泥浆以利于钻具的正常运转。为了降低钻井泥浆的滤失量以及钻井泥浆的表观粘度,通常情况下是加入由膪纶和水反应生成的水解聚丙烯膪铵盐,以其作为钻井助剂,可明显降低钻井泥浆的滤失量和泥浆的表观粘度。但用水解聚丙烯腈铵盐作为钻井助剂还存在一些不足之处。其一是氷解聚丙烯铵盐在生产过程中霈有较大的压力(通常反应压力窬控制在(2.1Mpa左右),因而其生产时的安全性较低。再则,水解聚丙烯腈铵盐的抗滤失抗表观粘度性能还有待进一步提高。
技术实现思路
为解决上述现有的缺点,本专利技术的主要目的在于提供一种实用的含聚丙烯铵盐的石油钻井助剂及其制造方法,进一步降低泥浆的滤失量及其表观粘度.避免了水解聚丙烯腈铵盐必须在较大(2.1Mpa左右)压力条件下方能进行生产所带来的不安全隐患,减少泥浆中助剂的使用量,提高了产品的效价比,从而有效地降低了钻井成本。为达成以上所述的目的,本专利技术的一种含聚丙烯铵盐的石油钻井助剂及其制造方法,采取以下的技术方案:一种含聚丙烯铵盐的石油钻井助剂及其制造方法,其特征在于,含有下述重量份比的组分:腈纶100-200份、水600-800份、聚丙烯酸盐7-12份、聚丙烯酰胺0.8-1.2份、交联剂5-10份、楠木粉50-60份。包括以下步骤:A、按所述重量份比称取各组分;B、将腈纶、水、聚丙烯酸盐、聚丙烯酰胺、交联剂置于反应釜中,混合后加热200-220Mpa,压力为1.2-1.5、恒温8-12小时 ...
【技术保护点】
一种含聚丙烯铵盐的石油钻井助剂及其制造方法,其特征在于 , 含有下述重量份比的组分 :腈纶 100‑200 份、水 600‑800 份、聚丙烯酸盐 7‑12 份、聚丙烯酰胺 0.8‑1.2 份、交联剂 5‑10 份、楠木粉 50‑60 份。
【技术特征摘要】
1.一种含聚丙烯铵盐的石油钻井助剂及其制造方法,其特征在于,含有下述重量份比的组分:腈纶100-200份、水600-800份、聚丙烯酸盐7-12份、聚丙烯酰胺0.8-1.2份、交联剂5-10份、楠木粉50-60份。2.根据权利要求1所述的一种含聚丙烯铵盐的石油钻井助剂及其制造方法,其特征在于,包括以下步骤:A、按...
【专利技术属性】
技术研发人员:陈晓洲,
申请(专利权)人:江苏常州酞青新材料科技有限公司,
类型:发明
国别省市:江苏,32