一种不锈钢粉末金相腐蚀液及其腐蚀方法技术
Stainless steel powder metallographic etching liquid and corrosion method thereof
Stainless steel powder metallographic etching liquid and corrosion method thereof. The metallographic corrosion liquid is composed of concentrated hydrochloric acid 5~10%, concentrated nitric acid 3~5% and anhydrous ethanol 85~92% according to the volume percentage. The corrosion method of the metallographic corrosion liquid of the stainless steel powder is to add the corrosive liquid to the surface of the sample to be tested. After the 1~10min is kept, the 1min is washed with water, and then the sample is dried and dried by alcohol. Metallographic etching liquid of the invention is applicable to all the corrosion of stainless steel powder, stainless steel powder corrosion metallographic sample preparation method is suitable for different size and different grades, the corrosion process stable, corrosion effect is good, can clearly observe the microstructure of samples.
【技术实现步骤摘要】
一种不锈钢粉末金相腐蚀液及其腐蚀方法
本专利技术涉及一种用于不锈钢粉末的金相腐蚀液配方及其腐蚀方法。
技术介绍
不锈钢块状样品金相组织通常采用王水进行腐蚀，王水的比例为盐酸:硝酸为3:1。不锈钢粉末金相组织大多采用跟块状样品相同的腐蚀液，即将腐蚀液滴到样品表面进行腐蚀。但是，由于粉末样品本身的特性，采用与块状样品相同的腐蚀液，往往达不到需要的效果。不锈钢粉末样品用王水腐蚀，样品表面马上冒泡腐蚀，腐蚀终点没有办法掌握，样品很快过腐蚀。而且，王水的腐蚀性非常强，在腐蚀的过程中，稍有不慎，沾染到人身体上，会对人的身体产生伤害。所以需要研究一种适合不锈钢粉末样品的、且操作安全、腐蚀终点判定简单的腐蚀液及腐蚀方法。
技术实现思路
本专利技术的目的是提供一种组织显示效果好，适用于不锈钢粉末的金相腐蚀液。本专利技术的另一个目的是提供一种腐蚀过程平稳、腐蚀时间容易掌握的一种不锈钢粉末的金相腐蚀方法。本专利技术的金相腐蚀液按体积百分比由浓盐酸5~10%，浓硝酸3~5%和无水乙醇85~92%组成。优选的不锈钢粉末金相腐蚀液按体积百分比由8ml浓盐酸，7ml浓硝酸和85ml无水乙醇组成。本专利技术的金相腐蚀液的制备方法是先后将浓盐酸和浓硝酸倒入无水乙醇中，搅拌均匀后，静置2分钟即配置成所述金相腐蚀液。不锈钢粉末金相样品腐蚀方法是：将腐蚀液滴加到待测样品表面，保持1~10min后，用水冲洗1min，再使用酒精冲洗，吹干样品即可。本专利技术具有以下有益效果：以王水为基础，调整了盐酸和硝酸的比例，乙醇用来稀释盐酸和硝酸，使得腐蚀液在使用中更加安全，且腐蚀时间容易掌握，腐蚀效果更好。本专利...
【技术保护点】
一种不锈钢粉末金相腐蚀液，其特征是按体积百分比由浓盐酸5~10%，浓硝酸3~5%和无水乙醇85~92%组成。
【技术特征摘要】
1.一种不锈钢粉末金相腐蚀液，其特征是按体积百分比由浓盐酸5~10%，浓硝酸3~5%和无水乙醇85~92%组成。2.根据权利要求1所述的不锈钢粉末金相腐蚀液，其特征是按体积百分比由8ml浓盐酸，...