The present invention relates to a train track in oil, it is composed of the following parts by weight of raw materials: castor oil 60 ~ 80, 10 ~ 20 barium sulfonate, zinc naphthenate 0.5 ~ 2, 5 ~ 15 mg lanolin soap, twelve alkenyl succinic acid from 0.5 to 2, eighteen from 0.1 to 2 were prepared, first; castor oil added to a reaction kettle, heating to 150-180 Deg. C, adding lanolin magnesium soap, and stirred at this temperature for 1-2 hours, then cooled to 75-85 DEG C, adding barium sulfonate, calcium sulfonate, eighteen amine, twelve alkenyl succinic acid, zinc naphthenate, and stirred at this temperature for 1-3 hours, and then cooled to 40-50 C, filtering, namely; the invention has scientific components, convenient preparation, can make the train rail with short-term anti rust effect is excellent, the use of regular brushing the product of the invention, can greatly prolong the service life of the rail.
【技术实现步骤摘要】
一种火车轨道防锈油
本专利技术属于钢材防锈
，特别是一种火车轨道防锈油。
技术介绍
目前，中国铁路发展迅猛，但是火车轨道的保养措施有限，由于火车轨道均是位于室外环境，风霜雨雪很容易造成火车轨道的锈蚀，造成火车轨道寿命缩短的问题。火车轨道一般都是采用钢材进行制作，由于钢材中含有其他金属元素，在室外环境很容易发生锈蚀，而火车轨道又需要有一定的摩擦力，用一般的防锈油难免带来不可避免的意外发生，因此，研发一种专门针对火车轨道的，又可以起到防锈作用的防锈油十分重要。
技术实现思路
本专利技术的目的就是要解决目前火车轨道均是位于室外环境，在室外环境的影响下很容易产生锈蚀，而目前又没有合适的防锈油的问题，提供一种火车轨道防锈油。本专利技术的一种火车轨道防锈油，由下述重量份原料组成：蓖麻油60～80石油磺酸钡10～20环烷酸锌0.5～2羊毛脂镁皂5～15十二烯基丁二酸0.5～2十八胺0.1～2；制备时，先向反应釜中加入蓖麻油，升温至150-180℃，加入羊毛脂镁皂，并在此温度下搅拌1-2小时，冷却至75-85℃之后，加入石油磺酸钡、石油磺酸钙、十八胺、十二烯基丁二酸、环烷酸锌，...
【技术保护点】
一种火车轨道防锈油，其特征在于由下述重量份原料组成：蓖麻油 60～80 石油磺酸钡 10～20环烷酸锌 0.5～2 羊毛脂镁皂 5～15十二烯基丁二酸 0.5～2 十八胺 0.1～2；制备时，先向反应釜中加入蓖麻油，升温至150‑180℃，加入羊毛脂镁皂，并在此温度下搅拌1‑2小时，冷却至75‑85℃之后，加入石油磺酸钡、石油磺酸钙、十八胺、十二烯基丁二酸、环烷酸锌，并在此温度下搅拌1‑3小时，然后冷却至40‑50℃，过滤，即得。
【技术特征摘要】
1.一种火车轨道防锈油，其特征在于由下述重量份原料组成：蓖麻油60～80石油磺酸钡10～20环烷酸锌0.5～2羊毛脂镁皂5～15十二烯基丁二酸0.5～2十八胺0.1～2；制备时，先向反应釜中加入蓖麻油，升温至1...