Bio oil to produce humic acid fertilizer adhesive coating agent, the ratio of raw materials was 5 water: 10, 60 bio oil 80, urea 5 15, film 20, trace metal powder 5 fertilizer 1 5; production process in accordance with the ratio of raw materials, bio oil is added into the reaction kettle is heated to 50 95 C, addition of urea, at the speed of 20 200 rpm 15 stirred for 80 minutes, then add the film powder, trace element fertilizer, mixing evenly, then add water stirring emulsion to form a mixture of uniform; the reaction process is completed, and then by the centrifugal filter separating insoluble, reaction liquid filtered the humic acid fertilizer adhesive coating agent.
【技术实现步骤摘要】
热解生物油制取腐植酸肥料粘合包膜剂1.
本专利技术提供热解生物油制取腐植酸肥料粘合包膜剂，涉及化肥提质增效，尤其涉及氮磷钾缓释肥料的粘合包膜制剂和粘合包膜制剂的生产方法。2.
技术介绍
据相关统计，化肥投入约占农民进行种植业生产总投入的50％左右，发展中国家粮食增产中50％来自于化肥的作用。但目前我国当季氮肥利用率仅为20％～35％，磷肥的利用率为10％～20％，钾肥的利用率为30％～60％，远低于世界发达国家利用水平。肥料利用率低不仅造成资源的巨大浪费,还给人类赖以生存的环境造成了严重污染。为了解决肥料养分释放速率与植物养分吸收速率不吻合，提高肥料利用率的问题，20世纪初提出了缓释肥料的概念。缓控释肥料是指肥料养分释放速率缓慢，释放期较长，在作物的整个生长期都可以满足作物生长需求的肥料，是提高氮磷钾肥料利用率的有效手段，已经成为了肥料界研究领域中新的热点。缓控释肥料目前主要是包膜肥料，主要是用蜡、聚合物和硫磺进行包膜，也可以用沥青、硅酸盐水泥.磷酸镁铵等包膜，就是在粒状水溶性(速效)肥料表面涂覆半透水性或不透水性物质，使养分通过包膜的微孔、缝隙慢慢释放出来，或在...
【技术保护点】
热解生物油制取腐植酸肥料粘合包膜剂，其特征是原料配比为：清水5‑10，热解生物油60‑80，尿素5‑15，成膜胶粉5‑20、微量金属肥1‑5；生产工艺为按照原料配比，将生物油加入反应釜后加热到50‑95℃，加入尿素，在转速20‑200转/分搅拌反应15‑80分钟，然后加入成膜胶粉、微量元素肥搅拌均匀，再加入水强力搅拌乳化，形成均匀的混合液；反应过程完毕，再由离心过滤机分离出不溶物，滤出的反应液即为腐植酸肥料粘合包膜剂。
【技术特征摘要】
1.热解生物油制取腐植酸肥料粘合包膜剂，其特征是原料配比为：清水5-10，热解生物油60-80，尿素5-15，成膜胶粉5-20、微量金属肥1-5；生产工艺为按照原料配比，将生物油加入反应釜后加热到50-95℃，加入尿素，在转速20-200转/分搅拌反应15-80分钟，然后加入成膜胶粉、微量元素肥搅拌均匀，再加入水强力搅拌乳化，形成均匀的混合液；反应过程完毕，再由离心过滤机分离出不溶物，滤出的反应液即为腐植酸肥料粘合包膜剂。2.根据权利要求1所述的热解生物油制取腐植酸肥料粘合包膜剂，其特征在于反应釜为不锈钢或塘玻璃材料的反应釜；强力搅拌乳化的设备为胶体磨或强剪切乳化机。...