The present invention provides a method for removing iron ion in ammonium sulfate, which comprises the following steps: (1) with adding water mixing reactor, open the stirring and heating method, batch input of industrial ammonium sulfate; (2) to be industrial ammonium sulfate soluble after adding citric acid, stirring 20min, which added the citric acid and ammonium sulfate industry in the weight ratio of 1:2500; (3) using ammonia or sulfuric acid PH5.0 5.5; (4) stop stirring and heating valve closed, standing for 1 hours after filtration, the filtrate is cooled to 20 DEG C crystallization, centrifugal separation, crystallization, drying; the method has the advantages of convenient operation, can meet the the ammonium sulfate product, has wide application prospect.
【技术实现步骤摘要】
一种硫酸铵中去除铁离子的方法
本专利技术涉及一种杂质处理工艺，尤其是一种硫酸铵中去除铁离子的方法。
技术介绍
硫酸铵为无色结晶或白色颗粒，无气味，280℃以上分解。水中溶解度：0℃时70.6g，100℃时103.8g。不溶于乙醇和丙酮。0.1mol/L水溶液的pH为5.5。相对密度1.77。折光率1.521。硫酸铵主要用作肥料，适用于各种土壤和作物，还可用于纺织、皮革、医药等方面。由于硫酸铵中铵离子的存在，与铁离子形成络合物，不能通过沉淀方法除去，现阶段，硫酸铵中铁离子的去除，通常采用多次重结晶方法，但该方法能耗高，损失大。因此，寻找一种方便有效的去除硫酸铵中铁离子的方法具有非常重要的生产实践意义。
技术实现思路
本专利技术所要解决的技术问题在于提供一种硫酸铵中去除铁离子的方法。为解决上述技术问题，本专利技术的技术方案是：一种硫酸铵中去除铁离子的方法，具体步骤为：(1)带搅拌反应釜中加入纯水，打开搅拌及加热法，分批投入工业硫酸铵；(2)待工业硫酸铵全溶后，加入柠檬酸搅拌反应20min，其中，所加入的柠檬酸与工业硫酸铵的重量比为1：2500；(3)使用氨水和/或硫酸调节PH5.0－5.5；(4)停止搅拌并关闭加热阀，静置1小时后过滤，滤液浓缩至出现大量结晶，氨水调节PH5.0－5.5，冷却至20℃，甩干，烘干。优选的，上述硫酸铵中去除铁离子的方法，所述步骤(1)中纯水与工业硫酸铵的重量比为1.2：1。优选的，上述硫酸铵中去除铁离子的方法，所述步骤(4)中母液依次继续浓缩两次，在PH5.0－5.5条件下结晶，甩干分离干燥，残余母液回收或弃去。本专利技术的有益效果是...
【技术保护点】
一种硫酸铵中去除铁离子的方法，其特征在于：具体步骤为：(1)带搅拌反应釜中加入纯水，打开搅拌及加热法，分批投入工业硫酸铵；(2)待工业硫酸铵全溶后，加入柠檬酸搅拌反应20min，其中，所加入的柠檬酸与工业硫酸铵的重量比为1：2500；(3)使用氨水和/或硫酸调节PH5.0－5.5；(4)停止搅拌并关闭加热阀，静置1小时后过滤，滤液浓缩至出现大量结晶，氨水调节PH5.0－5.5，冷却至20℃，甩干，烘干。
【技术特征摘要】
1.一种硫酸铵中去除铁离子的方法，其特征在于：具体步骤为：(1)带搅拌反应釜中加入纯水，打开搅拌及加热法，分批投入工业硫酸铵；(2)待工业硫酸铵全溶后，加入柠檬酸搅拌反应20min，其中，所加入的柠檬酸与工业硫酸铵的重量比为1：2500；(3)使用氨水和/或硫酸调节PH5.0－5.5；(4)停止搅拌并关闭加热阀，静置1小时后过滤，滤液浓缩至出现...
【专利技术属性】
技术研发人员：林利成，苏学松，
申请(专利权)人：天津市科密欧化学试剂有限公司，
类型：发明
国别省市：天津,12
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。