一种碳纤维增强热固性塑料拉挤成型方法技术

本发明专利技术提供了碳纤维增强热固性塑料拉挤成型方法，其包含如下步骤：1)将碳纤维预放在碳纤维供给装置上并由导引装置拉出；2)碳纤维引出并进入树脂浸渍槽进行树脂浸渍，所述的树脂浸渍槽预先加入热固性树脂和固化剂；3)浸渍树脂的碳纤维进入预成型口模固化成型；4)经牵引装置牵引出来进入切割装置切割成制品。采用碳纤维增强热固性塑料的各项性能，使其韧性和弯曲度有显著地提高。

Carbon fiber reinforced thermosetting plastics pultrusion forming method

The present invention provides a carbon fiber reinforced thermosetting plastic pultrusion method, comprising the following steps: 1) the carbon fiber pre on carbon fiber supply device and is pulled out by the guiding device; 2) carbon fiber and lead into the resin impregnation tank was impregnated with resin, resin impregnation tank the pretreatment with thermosetting resin and curing agent; 3) carbon fiber impregnated into the pre forming die forming; 4) by pulling out into the traction device of cutting into products. The toughness and bending strength of the thermosetting fiber reinforced by carbon fiber are improved remarkably.

【技术实现步骤摘要】
一种碳纤维增强热固性塑料拉挤成型方法
本专利技术涉及复合材料领域，特别是涉及一种碳纤维增强热固性塑料拉挤成型方法。
技术介绍
碳纤维具有轻质高强、耐腐蚀、耐疲劳性、耐高温等许多优异的性能。在实际工程应用中，碳纤维增强各种树脂基体，形成适用于不同应用领域的碳纤维复合材料，如应用于航空航天或各种工业领域的碳纤维复合材料。其中，碳纤维复合材料的耐高温、抗火性能对其工程应用具有重要的影响，如航空航天复合材料需要抗高温、抗火；土木工程复合材料的耐高温与抗火性能也是影响其在重要建筑结构应用的关键性能。
技术实现思路
本专利技术的目的在于，针对现有技术的不足，提供一种碳纤维增强热固性塑料拉挤成型方法。本专利技术为实现上述目的所采用的技术方案为：一种碳纤维增强热固性塑料拉挤成型方法，其包含如下步骤：1)将碳纤维预放在碳纤维供给装置上并由导引装置拉出；2)碳纤维引出并进入树脂浸渍槽进行树脂浸渍，所述的树脂浸渍槽预先加入热固性树脂和固化剂；3)浸渍树脂的碳纤维进入预成型口模固化成型；4)经牵引装置牵引出来进入切割装置切割成制品。优选地，所述固化剂为甲基六氢邻苯二甲酸酐。优选地，热固性树脂与固化剂质量比为1∶本文档来自技高网...

【技术保护点】
一种碳纤维增强热固性塑料拉挤成型方法，其特征在于，其包含如下步骤：1)将碳纤维预放在碳纤维供给装置上并由导引装置拉出；2)碳纤维引出并进入树脂浸渍槽进行树脂浸渍，所述的树脂浸渍槽预先加入热固性树脂和固化剂；3)浸渍树脂的碳纤维进入预成型口模固化成型；4)经牵引装置牵引出来进入切割装置切割成制品。

【技术特征摘要】
1.一种碳纤维增强热固性塑料拉挤成型方法，其特征在于，其包含如下步骤：1)将碳纤维预放在碳纤维供给装置上并由导引装置拉出；2)碳纤维引出并进入树脂浸渍槽进行树脂浸渍，所述的树脂浸渍槽预先加入热固性树脂和固化剂；3)浸渍树脂的碳纤维进入预成型口模固化成型；4)经牵引装置牵引出来进入切割装置切割成制品。2.根据权利要求1所述的碳纤维增强热固性塑料拉挤成型方法，其特征在于，所述固化剂为甲基六氢邻苯二甲酸酐。3.根据权利要求1所述的碳纤维增强热固性塑料拉挤成型方法，其特征在于，热固性树脂与固化剂质量比为1∶1～1.5。4.根据权...

【专利技术属性】
技术研发人员：刘彦崇，
申请(专利权)人：广东延春高新材料科技股份有限公司，
类型：发明
国别省市：广东,44