The invention discloses a water-soluble adhesive for pressure-sensitive adhesive. The invention of the water soluble adhesive adhesive comprises the following components: the mass ratio of the main reducer 50 80, polyvinylpyrrolidone, 10 22 copies, 10 copies, 4 glycerol ethylene glycol 5 10 copies, three trihydroxymethylenepropane 5 10 copies, 24 copies, 10 caprolactam dehydration July 8 dilaudid sorbitol 27, polyoxyethylene oxypropylene oleate 2 9 copies, 15 copies of 5 preservatives. The water-soluble adhesive of the invention can be peeled and pasted repeatedly, and is suitable for pasting paper, labels and the like. Sticker adhesive of the invention can be quickly dissolved in water, and completely dissolved, not to leave any items stuck back.
【技术实现步骤摘要】
本专利技术涉及一种不干胶胶粘剂材料，属于化工原料
，具体是一种水溶性不干胶胶粘剂。
技术介绍
胶粘剂/粘接剂是一种常用的化工原料，目前已被广泛应用。现有的不干胶胶粘剂/粘接剂，为了获得加好的粘贴效果，其配方中加入了固化剂，而固化剂多为有机原料，不溶于水，当需要将不干胶去除时，此类胶粘剂/粘接剂不易全部去除，导致被粘物品，如纸张、墙面、家具表面等留下污渍和痕迹，影响物品的外表美观。
技术实现思路
本专利技术的目的是提供一种水溶性不干胶胶粘剂。本专利技术的技术方案如下：一种水溶性不干胶胶粘剂，是由以下质量配比的组分组成：主粘剂50-80份、聚乙烯基吡咯烷酮10-22份、丙三醇4-10份、乙二醇5-10份、三羟甲基丙烷5-10份、己内酰胺10-24份、失水山梨醇月桂酸酯8-27份、聚氧乙烯氧丙烯油酸酯2-9份、防腐剂5-15份。进一步的，所述主粘剂为阿拉伯树胶、海藻酸钠、明胶，其质量比为5-15:5-10:10-30。更进一步的，所述防腐剂为苯甲酸钠或山梨酸钠。优选的，所述水溶性不干胶胶粘剂是由以下质量配比的组分组成：阿拉伯树胶12份、海藻酸钠10份、明胶25份、聚乙烯基吡咯烷酮14份、丙三醇7份、乙二醇10份、三羟甲基丙烷6份、己内酰胺20份、失水山梨醇月桂酸酯19份、聚氧乙烯氧丙烯油酸酯4份、山梨酸钠12份。更优选的，所述水溶性不干胶胶粘剂是由以下质量配比的组分组成：阿拉伯树胶12份、海藻酸钠10份、明胶25份、聚乙烯基吡咯烷酮20份、丙三醇8份、乙二醇5份、三羟甲基丙烷10份、己内酰胺15份、失水山梨醇月桂酸酯20份、聚氧乙烯氧丙烯油酸酯5份、苯甲酸钠...
【技术保护点】
一种水溶性不干胶胶粘剂，其特征在于：由以下质量配比的组分组成：主粘剂 50‑80份、聚乙烯基吡咯烷酮10‑22份、丙三醇4‑10份、乙二醇5‑10份、三羟甲基丙烷5‑10份、己内酰胺10‑24份、失水山梨醇月桂酸酯8‑27份、聚氧乙烯氧丙烯油酸酯2‑9份、防腐剂 5‑15份。
【技术特征摘要】
1.一种水溶性不干胶胶粘剂，其特征在于：由以下质量配比的组分组成：主粘剂50-80份、聚乙烯基吡咯烷酮10-22份、丙三醇4-10份、乙二醇5-10份、三羟甲基丙烷5-10份、己内酰胺10-24份、失水山梨醇月桂酸酯8-27份、聚氧乙烯氧丙烯油酸酯2-9份、防腐剂5-15份。2.根据权利要求1所述的水溶性不干胶胶粘剂，其特征在于：所述主粘剂为阿拉伯树胶、海藻酸钠、明胶，其质量比为5-15:5-10:10-30。3.根据权利要求1所述的水溶性不干胶胶粘剂，其特征在于：所述防腐剂为苯甲酸钠或山梨酸钠。4.根据权利要求1所述的水溶...
【专利技术属性】
技术研发人员：邓平，
申请(专利权)人：惠州市泽信实业有限公司，
类型：发明
国别省市：广东;44