一种含FB的聚氨酯人造革阻燃组合物及制造方法技术

本发明专利技术涉及一种含FB的聚氨酯人造革阻燃组合物，主要包括如下质量份数的组分：聚氨酯 60～80份，FB 10～15份，锌粉 0.2～0.5份，无机填料5～25份。阻燃组合物的制造方法是将上述原料熔融混合，由行星挤出机挤出，冷却后得到。本发明专利技术中的聚氨酯人造革具有成分简单，对设备无腐蚀，环境友好等优点。

Polyurethane artificial leather flame retardant composition containing FB and manufacturing method thereof

The present invention relates to FB containing polyurethane artificial leather flame retardant composition, quality mainly includes the following components: Polyurethane 60 ~ 80, 10 ~ 15 FB, zinc from 0.2 to 0.5, 5 to 25 portions of inorganic filler. The flame retardant composition is prepared by melting and mixing the raw material, extruded by a planetary extruder, and obtained after cooling. The polyurethane artificial leather of the present invention has the advantages of simple composition, no corrosion to the equipment and friendly environment.

【技术实现步骤摘要】
一种含FB的聚氨酯人造革阻燃组合物及制造方法
本专利技术属于聚氨酯人造革
，具体涉及聚氨酯人造革的阻燃组合物及制造方法。
技术介绍
聚氨酯树脂具有柔软性、结合力强，耐磨，耐油，抗酶菌等优良的性能，从而广泛应用于机械、电子/电气等领域。随着近年来人们对于阻燃剂毒性及安全等方面的日益关注，无卤阻燃剂越来越广泛地应用。聚氨酯在制备过程中，部分添加物质在加工温度下趋于分解或降解，这些分解或降解产物可腐蚀挤压机筒体、模塑机表面、螺杆及其他熔融加工设备。
技术实现思路
本专利技术所要解决的技术问题是针对上述现有技术提供一种含FB（硼酸盐）的聚氨酯人造革阻燃组合物及相应的制造方法，成分简单，减少生产污染，保护加工设备。本专利技术解决上述问题所采用的技术方案为：一种含FB的聚氨酯人造革阻燃组合物，主要包括如下质量份数的组分聚氨酯60～80份，FB10～15份，锌粉0.2～0.5份，无机填料5～25份。优选地，所述无机填料为：玻璃纤维、玻璃薄片、高岭土、粘土、滑石、钙硅石、碳酸钙、二氧化硅、碳纤维或钛酸钾中的一种或两种以上的混合物。较合理的是，所述组合物中还包括稳定剂、抗氧剂、润滑剂、颜料、脱模机、本文档来自技高网...

【技术保护点】
一种含FB的聚氨酯人造革阻燃组合物，其特征在于：主要包括如下质量份数的组分：聚氨酯 60～80份，FB 10～15份，锌粉 0.2～0.5份，无机填料5～25份。

【技术特征摘要】
2015.11.19 CN 20151079855831.一种含FB的聚氨酯人造革阻燃组合物，其特征在于：主要包括如下质量份数的组分：聚氨酯60～80份，FB10～15份，锌粉0.2～0.5份，无机填料5～25份。2.根据权利要求1所述的含FB的聚氨酯人造革阻燃组合物，其特征在于：所述无机填料为：玻璃纤维、玻璃薄片、高岭土、...

【专利技术属性】
技术研发人员：季建良，
申请(专利权)人：无锡华联塑料制品有限公司，
类型：发明
国别省市：江苏,32