The present invention relates to the technical field of polyester fiber, in particular to a negative ion polyester fiber, in accordance with the mass fraction meter comprises the following components: polyester fiber slice 20-30, negative ion additive 5-12, 5-10 polyamide resin, silane coupling agent 3-8, ultra disperse negative ion powder 10-15, nano antibacterial agent 20-35. Far infrared emission agent 8-13, phosphite 4-10. Using the above formula, negative ion polyester fiber of the invention, the use of good performance, negative ion concentration is high, wide range of applications; in addition, the operation method, preparation of negative ion polyester fiber of the invention is simple and convenient for popularization and application.
【技术实现步骤摘要】
一种负离子聚酯纤维
本专利技术涉及聚酯纤维
,特别是一种负离子聚酯纤维。
技术介绍
聚酯纤维由有机二元酸和二元醇缩聚而成的聚酯经纺丝所得的合成纤维。工业化大量生产的聚酯纤维是用聚对苯二甲酸乙二醇酯制成的,中国的商品名为涤纶。是当前合成纤维的第一大品种。涤纶的生产过程包括缩聚和熔体纺丝两部分。原料主要从石油裂解获得,也可从煤和天然气取得。石油加热裂解得到甲苯、二甲苯和乙烯等,经化学加工后可得到对苯二甲酸或对苯二甲酸二甲酯及乙二醇。在早期涤纶生产中由于对苯二甲酸不易精制,曾用对苯二甲酸二甲酯和乙二醇为原料。
技术实现思路
本专利技术需要解决的技术问题是提供一种负离子聚酯纤维。为解决上述的技术问题,本专利技术的一种负离子聚酯纤维,按照质量份数计包括以下组分:聚酯纤维切片20-30份,负离子母粒5-12份,聚酰胺树脂5-10份,硅烷偶联剂3-8份,超分散负离子粉10-15份,纳米抗菌剂20-35份,远红外线发射剂8-13份,亚磷酸酯4-10份。进一步的,按照质量份数计包括以下组分:聚酯纤维切片20份,负离子母粒5份,聚酰胺树脂5份,硅烷偶联剂3份,超分散负离子粉10份,纳米抗菌剂20份,远红外线发射剂8份,亚磷酸酯4份。进一步的,按照质量份数计包括以下组分:聚酯纤维切片30份,负离子母粒12份,聚酰胺树脂10份,硅烷偶联剂8份,超分散负离子粉15份,纳米抗菌剂35份,远红外线发射剂13份,亚磷酸酯10份。进一步的,按照质量份数计包括以下组分:聚酯纤维切片23份,负离子母粒9份,聚酰胺树脂6份,硅烷偶联剂5份,超分散负离子粉12份,纳米抗菌剂25份,远红外线发射剂 ...
【技术保护点】
一种负离子聚酯纤维,其特征在于,按照质量份数计包括以下组分:聚酯纤维切片20‑30份,负离子母粒5‑12份,聚酰胺树脂5‑10份,硅烷偶联剂3‑8份,超分散负离子粉10‑15份,纳米抗菌剂20‑35份,远红外线发射剂8‑13份,亚磷酸酯4‑10份。
【技术特征摘要】
1.一种负离子聚酯纤维,其特征在于,按照质量份数计包括以下组分:聚酯纤维切片20-30份,负离子母粒5-12份,聚酰胺树脂5-10份,硅烷偶联剂3-8份,超分散负离子粉10-15份,纳米抗菌剂20-35份,远红外线发射剂8-13份,亚磷酸酯4-10份。2.按照权利要求1所述的一种负离子聚酯纤维,其特征在于,按照质量份数计包括以下组分:聚酯纤维切片20份,负离子母粒5份,聚酰胺树脂5份,硅烷偶联剂3份,超分散负离子粉10份,纳米抗菌剂20份,远红外线发射剂8份,亚磷酸酯4份。3.按照权利要求1所述的一种负离子聚酯纤维,其特征在于,按照质量份数计包括以下组分:聚酯纤维切片30份,负...