The invention discloses a truck glass steel and its preparation method, it uses the following raw materials in parts by weight: glass fiber yarn 30 ~ 40, 10 ~ 15 of epoxy resin and nano tea powder 0.5 ~ 1 nm, 1 calcareous shale ~ 5, 1 ~ 5 of hydrogenated rosin two, a silicon oxide 1 ~ 5, 1 ~ 5 boric acid and ethylenediamine 1 ~ 5, 1 ~ 5 ps and water 1 ~ 10; including the raw material proportioning and mixing, foaming, curing stage 3, pultrusion traction. The invention is mainly by adding nano tea powder, nano calcareous shale, hydrogenated rosin, boric acid, polystyrene foaming stage and control temperature and time, so as to improve the product of acid corrosion and high temperature impact resistance, rigidity, heat resistance, aging resistance and scratch resistance properties.
【技术实现步骤摘要】
卡车玻璃钢及其制备方法
本专利技术涉及新材料
,尤其是一种卡车专用的玻璃钢。
技术介绍
在卡车的生产过程中,经过用到玻璃钢材料,例如卡车的导流罩主要采用的就是玻璃罩,其要求具备优异的耐酸腐蚀、高低温冲击性、刚性、耐热性、耐老化性及耐刮擦性性能。然而,随着汽车行业的不断发展,其对卡车玻璃钢综合性能的要求也越来越高。
技术实现思路
本专利技术的目的是提供一种卡车玻璃钢及其制备方法,从而提高现有卡车玻璃钢综合性能。为了解决上述技术问题,本专利技术所采用的技术方案是:采用以下重量份数的原料:玻璃纤维纱30份~40份、环氧树脂10份~15份、纳米级茶叶粉末0.5份~1份、纳米钙质页岩1份~5份、氢化松香1份~5份、二氧化硅1份~5份、硼酸1份~5份、乙二胺1份~5份、聚苯乙烯1份~5份以及水1份~10份;其制备方法包括以下步骤:A、按配比称取上述原料,并高速混合搅拌3~5min;B、将步骤A得到的混合物进行发泡、固化,然后进行拉挤牵引;其中,发泡过程分为3个阶段,每个阶段均为5分钟~10分钟,且这三个阶段的温度依次为30℃~40℃、50℃~60℃以及30℃~40℃。由于采用上述技术方案,本专利技术得到的有益效果是:(1)本专利技术主要通过添加纳米级茶叶粉末、纳米钙质页岩、氢化松香、硼酸以及聚苯乙烯,从而提高产物耐酸腐蚀性、高低温冲击性、刚性、耐热性、耐老化性及耐刮擦性等性能。(2)本专利技术通过将制备过程中的发泡过程分为三个阶段,并分别对这三个发泡阶段的温度和时间进行限定,从而优化产物的综合性能。具体实施方式以下结合具体实施例对本专利技术作进一步详述,而本专利技术 ...
【技术保护点】
一种卡车玻璃钢,其特征在于由以下重量份数的原料制成:玻璃纤维纱30份~40份、环氧树脂10份~15份、纳米级茶叶粉末0.5份~1份、纳米钙质页岩1份~5份、氢化松香1份~5份、二氧化硅1份~5份、硼酸1份~5份、乙二胺1份~5份、聚苯乙烯1份~5份以及水1份~10份。
【技术特征摘要】
1.一种卡车玻璃钢,其特征在于由以下重量份数的原料制成:玻璃纤维纱30份~40份、环氧树脂10份~15份、纳米级茶叶粉末0.5份~1份、纳米钙质页岩1份~5份、氢化松香1份~5份、二氧化硅1份~5份、硼酸1份~5份、乙二胺1份~5份、聚苯乙烯1份~5份以及水1份~10份。2.一种卡车玻璃钢的制备方法,其特征在于:采用以下重量份数的原料:玻璃纤维纱30份~40份、环氧树脂10份~15份、纳米级茶叶粉末0.5份...