一种封头的清洗方法技术
Method for cleaning head
The invention relates to a cleaning method of a head cover, which is characterized in that the method comprises the following steps: (1) the head cap is sprayed with an organic matter detergent to lay 30min at a temperature of between 20 and 45 DEG C. (2) the head is immersed in the sodium borate solution of 3%, and (3) the head is immersed in a compound surfactant to be treated. The advantages of the invention are: simple operation, convenient maintenance, long range effect, good cleaning quality, high efficiency, good compatibility, the process parts after surface cleaning clean, does not affect the part precision and surface state, non-toxic, no smell, no harm to the health of operation.
【技术实现步骤摘要】
本专利技术主要涉及一封头,尤其涉及一种封头的清洗方法。
技术介绍
封头，是石油化工、原子能到食品制药诸多行业压力容器设备中不可缺少的重要部件，主要用于各种容器设备，材质主要是以不锈钢、碳钢、合金钢、铝、钛、铜、镍及镍合金等。在压力容器中封头的材料主要以铝合金为主。不锈钢封头在制作成形、焊接、施工等过程中会带来表面油污、铁锈、非金属脏物等，影响了封头的使用寿命，因此要处理表面污垢，以免在实用过程中导致封头不能正常使用。
技术实现思路
本专利技术的目的是克服上述现有工艺存在的不足，而提供一种封头的清洗方法。本专利技术的技术方案是：清洁封头的制作方法，其步骤为：将封头喷淋有机物助洗剂在温度为20—45℃下放置30min，之后在用清水冲洗。将封头浸泡在3％的硼酸钠溶液进行处理，处理温度为20—55℃，处理时间为15-25min，之后用清水冲洗。将封头浸泡复合表面活性剂进行处理，处理温度为20-50℃，处理时间为30min，之后，再用清水冲洗。本专利技术的优点是：操作简便、效程持久、使用维护方便、清洗质量好、效率高、工艺兼容性好、经清洗后的零件表面洁净、不影响零件的尺寸精度和表面状态、无毒、无刺激性气味、不危害操作者身体健康。具体实施例下面结合一个实施例，对本专利技术提供一种封头的清洗方法进行详细的说明。清洁封头的制作方法，其步骤为：将封头喷淋有机物助洗剂在温度为20—45℃下放置30min，之后在用清水冲洗。将封头浸泡在3％的硼酸钠溶液进行处理，处理温度为20—55℃，处理时间为15-25min，之后用清水冲洗。将封头浸泡复合表面活性剂进行处理，处理温度为20-50...
【技术保护点】
一种封头的清洗方法，其特征在于步骤为：包括以下步骤：(1)将封头喷淋有机物助洗剂在温度为20—45℃下放置30min，之后在用清水冲洗。(2)将封头浸泡在3％的硼酸钠溶液进行处理，处理温度为20—55℃，处理时间为15‑25min，之后用清水冲洗。(3)将封头浸泡复合表面活性剂进行处理，处理温度为20‑50℃，处理时间为30min，之后，再用清水冲洗。
【技术特征摘要】
1.一种封头的清洗方法，其特征在于步骤为：包括以下步骤：(1)将封头喷淋有机物助洗剂在温度为20—45℃下放置30min，之后在用清水冲洗。(2)将封头浸泡在3％的硼酸钠溶液进行...
【专利技术属性】
技术研发人员：季振宽，
申请(专利权)人：青岛旭升封头有限公司，
类型：发明
国别省市：山东;37