The invention discloses a surface enhanced Raman scattering substrate for detection of pesticide and preparation method and application thereof, the substrate comprises a substrate, a titanium thin film layer covered on the substrate surface, covered on the silver film layer of titanium film surface layer, and covered on the silver nanorod array film layer on the surface layer of silver, and silver angle nanorods with glass surface is 86 DEG; through cleaning the substrate, preparation of titanium, silver coating preparation of silver nanorod array layer so as to obtain the invented, applied to the detection of pesticides, especially suitable for the rapid detection of food safety problems.
【技术实现步骤摘要】
本专利技术涉及一种表面增强拉曼散射的基底及其制备方法，以及基于该基底的农药检测的应用，属食品安全检测
技术介绍
如今，农药、食品添加剂的过量添加与残留严重威胁着人们的食品安全。其中：农药这类存在着高毒性风险的化工产品，其在蔬菜水果中的使用一直存在着残留问题。现有的检测方法普遍存在样品前处理过程复杂、检测费用昂贵、检测时间较长和相对误差较大等问题，对检测使用广泛的农药存在着无法在线实时监测、易受外界环境影响等问题。目前，表面增强拉曼光谱技术作为一种高灵敏的检测技术，其扩展了表面振动光谱，为大量的化学检测问题提供了可能性的解决办法。表面增强拉曼效应的基本原理主要分为化学增强机理与电磁增强机理。物理增强主要由于外加电场使金属表面等离子体共振引起表面局域电场增强而产生拉曼信号的增强；化学增强往往通过电荷转移，粗糙金属表面吸附分子后分子的极化率产生变化，若分析吸附于金属纳米离子表面时，就会产生较强的等离子体共振，从而增强了拉曼散射信号。在检测的实际应用中，对理想的SERS基板具有较高的要求，如：增强性能高，可重复性好，统一性强，寿命稳定，制造简单，成本低。而目前...
【技术保护点】
一种检测农药的表面增强拉曼散射基底，其特征在于，包括基片，覆盖于基片表面的钛薄膜层，覆盖于钛薄膜层表面的银薄膜层，以及覆盖于银薄膜层表面的银纳米棒阵列层，且银纳米棒与玻璃片表面的夹角为86°。
【技术特征摘要】
1.一种检测农药的表面增强拉曼散射基底，其特征在于，包括基片，覆盖于基片表面的钛薄膜层，覆盖于钛薄膜层表面的银薄膜层，以及覆盖于银薄膜层表面的银纳米棒阵列层，且银纳米棒与玻璃片表面的夹角为86°。2.根据权利要求1所述的基底，其特征在于，所述的银纳米棒的棒长为850-950nm、直径为80-99nm、棒间距为150-300nm。3.根据权利要求1或2所述的基底，其特征在于，所述的基片为硅晶片或玻璃片。4.根据权利要求1或2所述的基底，其特征在于，所述的钛薄膜层的厚度为20nm。5.根据权利要求1或2所述的基底，其特征在于，所述的银薄膜层的厚度为100nm。6.一种根据权利要求1-5任一所述基底的制备方法，其特征在于，包括如下具体步骤：A、清洗基片：先配制洗液清洗基片，然后用去离子水冲洗干净，氮气吹干，固定在真空沉积室中；B、制备钛、银薄膜层：在压力小于1×10-6Tor...
【专利技术属性】
技术研发人员：姚悦，韩彩芹，邹琦，王稳，孙佳炜，雷金燕，
申请(专利权)人：江苏师范大学，
类型：发明
国别省市：江苏;32