The present invention provides a polymer mortar composite material and its preparation method, using the raw materials after grinding and mixing the raw materials include mineral material and composite modifier; aggregate comprises nosean, pearl stone and iron slag; the composite modifier comprises a solid sodium silicate, polyacrylamide, formaldehyde prepolymer and water. The invention adopts organic polymer modification of geopolymer, which makes the change of mortar materials has good fluidity, and complex organic molecules between the mortar materials have the characteristics of high early strength, increase the strength and toughness of final products and density. The invention can effectively deal with the mineral tailings containing ferrochrome slag of toxic heavy metal ions, effective curing metal chromium ions, reducing the dissolution rate of chromium ion, reducing the waste of land resources, mineral material waste into green building materials.
【技术实现步骤摘要】
本专利技术属于道路工程材料领域，涉及地质聚合物，具体涉及一种地聚物复合胶浆材料及其制备方法。
技术介绍
地质聚合物(Geopolymer)这一概念最早由法国J.Dvidovits提出，地质聚合物是一种由硅氧四面体和铝氧四面体聚合而成的具有非晶态或者准晶态的铝硅酸盐无机聚合物材料。与传统水泥材料相比，地质聚合物制品具有力学性能好，耐高温，耐腐蚀，可固定金属离子、核废料及有害废料等优点，同时其制备过程中的能耗量及二氧化碳排放量均低于普通硅酸盐水泥。在目前我国大力推行“资源节约型、环境友好型”双型社会的大环境下，发展性能高、低碳环保、实际可操作的地聚合物材料具有重要的现实意义。地质聚合物材料抗压性能优良但抗折强度较低，研究者根据地质聚合物使用需求不同会适当的对其进行改性处理。目前地质聚合物改性研究主要集中于聚丙烯束状单丝纤维、短切碳纤维、玄武岩等纤维增韧；亦有部分学者采用有机物进行地质聚合物改性，但其改性材料多为单一有机物，忽略了有机高分子交联作用对地聚合物复合作用。因此，亟需研发一种综合性能优良的地质聚合物复合胶浆材料。
技术实现思路
针对现有技术存在的不足，本专利技术...
【技术保护点】
一种地聚物复合胶浆材料，其特征在于，采用以下原料制成：所述的原料包括矿料和复合改性剂；所述的矿料包括黝方石、珍珠石和铬铁矿渣；所述的复合改性剂包括固体硅酸钠、聚丙烯酰胺、酚醛预聚物和水。
【技术特征摘要】
1.一种地聚物复合胶浆材料，其特征在于，采用以下原料制成：所述的原料包括矿料和复合改性剂；所述的矿料包括黝方石、珍珠石和铬铁矿渣；所述的复合改性剂包括固体硅酸钠、聚丙烯酰胺、酚醛预聚物和水。2.如权利要求1所述的地聚物复合胶浆材料，其特征在于，以重量份数计，所述的矿料由以下原料组成：珍珠石为30～40份，黝方石为30～40份，铬铁矿渣为20～40份，矿料中原料的重量份数之和为100份。3.如权利要求2所述的地聚物复合胶浆材料，其特征在于，以重量分数计，矿料为100份，固体硅酸钠为20份，聚丙烯酰胺为5～12份，酚醛预聚物为0～5份，水为26～30份。4.如权利要求3所述的地...
【专利技术属性】
技术研发人员：王朝辉，张廉，陈谦，高志伟，王新岐，狄升贯，张磊，
申请(专利权)人：长安大学，
类型：发明
国别省市：陕西;61
还没有人留言评论。发表了对其他浏览者有用的留言会获得科技券。