The invention discloses a nickel sulfate solution from the depth of copper removal method, the method comprises the following steps: nickel sulfate solution containing copper heating, the heating temperature is 40 to 80 DEG C, then adding soluble sulfur cyanide, reducing agent, mixing, reaction time is 10min ~ 4h, complete the solid-liquid separation after reaction removal of copper. The method of the invention has the advantages of simple operation, small amount of adding reagent, wide range of adaptation to acidity, high mass ratio of copper and nickel in the slag to more than 30, small amount of slag, stable effect, etc..
【技术实现步骤摘要】
本专利技术涉及有色冶金
,更具体涉及一种从硫酸镍溶液中深度除铜的方法。
技术介绍
镍应用于不锈钢、电池材料、储氢材料、磁性材料、触媒、形态记忆合金等。由于铜镍伴生等缘故,镍矿中或多或少含有一定量的铜,镍溶出时铜进入溶液。铜的还原电位高于镍的还原电位,电解时铜与镍同时析出,产品中铜含量难以满足要求,阴极镍质量下降。为了降低镍中铜的含量,需要对镍电解液进行深度净化除铜。截至目前,从硫酸镍溶液中除铜基本上采用的是硫化沉淀除铜的常规思路,使用试剂为硫化氢、硫化钠、硫化镍、硫代碳酸镍、硫化锰、活性硫化镍、纳米硫化镍等。采用上述硫化试剂除铜时,即使硫酸浓度<20g/L,也产生硫化氢,污染环境;上述硫化试剂中如硫化钠难以控制局部pH,渣中镍铜质量比高;硫化镍、活性硫化镍存在被包裹,同样渣中铜镍质量比低,一般Cu:Ni<20:1;而硫化锰引入锰金属离子;纳米硫化镍除铜效果好,但纳米硫化镍制备时过滤困难且易氧化难保存,成本高。另外,工业化的除铜后液中往往要求铜的浓度<2.5mg/L;而现有技术的很多方法,有的可能根本达不到,有的则达到后又存环境污染等问题,这也使得现有技术人员很是苦恼。因此,急需开发一种对镍电解液进行深度净化除铜的方法。
技术实现思路
(一)要解决的技术问题本专利技术要解决的技术问题就是如何深度除去硫酸镍溶液中的铜,同时减少污染,降低成本,而提供一种从硫酸镍溶液中深度除铜的方法。(二)技术方案为了解决上述技术问题,本专利技术提供了一种从硫酸镍溶液中深度除铜的方法,该方法包括步骤:将含铜的硫酸镍溶液加热,加热温度为40℃~80℃,然后加入 ...
【技术保护点】
一种从硫酸镍溶液中深度除铜的方法,其特征在于,该方法包括步骤:将含铜的硫酸镍溶液加热,加热温度为40℃~80℃,然后加入可溶性硫氰化物,还原剂,搅拌,反应时间为10min~4h,反应完全后固液分离除去铜。
【技术特征摘要】
1.一种从硫酸镍溶液中深度除铜的方法,其特征在于,该方法包括步骤:将含铜的硫酸镍溶液加热,加热温度为40℃~80℃,然后加入可溶性硫氰化物,还原剂,搅拌,反应时间为10min~4h,反应完全后固液分离除去铜。2.根据权利要求1所述的从硫酸镍溶液中深度除铜的方法,其特征在于,所述的硫酸镍溶液为将硫酸镍固体溶解后得到的硫酸镍溶液、初步分离铜镍后的镍浸出液或硫酸镍电解液。3.根据权利要求1所述的从硫酸镍溶液中深度除铜的方法,其特征在于,在所述的硫酸镍溶液中,镍的浓度为10~100g/L,铜的浓度为0.01g/L~4g/L。4.根据权利要求1所述的从硫酸镍溶液中深度除铜的方法,其特征在于,所述的可溶性硫氰化物为KSCN、NaSCN或NH4SCN。5.根据权利要求1所述...